Effect of chemical milling on low-cycle fatigue behavior of an Al-Mg-Si alloy

被引：11
作者：
Spear, Ashley D. [1 ]
Ingraffea, Anthony R. [1 ]
机构：
[1] Cornell Univ, Sch Civil & Environm Engn, Ithaca, NY 14853 USA
来源：
CORROSION SCIENCE | 2013年 / 68卷
基金：
美国国家科学基金会;
关键词：
Aluminum; SEM; Alkaline corrosion; Corrosion fatigue; Pitting corrosion; PITTING CORROSION; ALUMINUM-ALLOY; CRACK GROWTH; SURFACE-ROUGHNESS; INITIATION; CRYSTALLOGRAPHY; DAMAGE;
D O I：
10.1016/j.corsci.2012.11.006
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of alkaline chemical milling used for dimensionally reducing aluminum-alloy structures is assessed in terms of total fatigue life and crack-initiation mechanisms. Chemically milled Al-Mg-Si specimens exhibited a 50% reduction in average fatigue lives compared to electropolished Al-Mg-Si specimens at comparable peak-applied loads above macroscopic yield. The fatigue-life reduction of the chemically milled specimens is likely associated with early onset of crack initiation due to pit-induced-stress concentrations. Fractographic analyses suggest a transition in the crack-initiation mechanisms from predominantly {111}-slip plane cracking to partly or predominantly pit-induced-stress driven depending on the depth of surface pits. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：144 / 153
页数：10
相关论文
共 52 条
  • [1] *AM SOC MET, 1985, MET MICR, V9
  • [2] [Anonymous], 2000, S0812000 ANSIAIAA
  • [3] [Anonymous], 2002, UND EXTR AL ALL ALL
  • [4] [Anonymous], 2010, 251782 ISOFDIS
  • [5] ASTM International, 2011, E811 ASTM INT
  • [6] EFFECT OF SURFACE FINISH ON FATIGUE-STRENGTH
    BAYOUMI, MR
    ABDELLATIF, AK
    [J]. ENGINEERING FRACTURE MECHANICS, 1995, 51 (05) : 861 - 870
  • [7] Beeson H. D, 2002, TP2002210769 NASA
  • [8] Bray G., 1997, ASTM STP, V1298
  • [9] Driving forces for localized corrosion-to-fatigue crack transition in Al-Zn-Mg-Cu
    Burns, J. T.
    Larsen, J. M.
    Gangloff, R. P.
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2011, 34 (10) : 745 - 773
  • [10] Effect of corrosion severity on fatigue evolution in Al-Zn-Mg-Cu
    Burns, James T.
    Kim, Sangshik
    Gangloff, Richard P.
    [J]. CORROSION SCIENCE, 2010, 52 (02) : 498 - 508
123456