The relationship between photo-catalytic performance and optical property over Si-incorporated TiO2

This study focuses on the relationship between photo-catalytic performance and optical property over Si-incorporated TiO2. The Si-incorporated TiO2 particles exhibited a pure structure of anatase having a particle size of less than 20 nm and surface area of more than 190 m(2)/g. The absorbance did not shift to a higher wavelength in spite of the incorporation of the Si ions, but the intensity of the photoluminescence (PL) curve was the smallest in the case of the 2.0 mol% Si-TiO2, which was related to the recombination between the excited electrons and holes. Based on these results, the photodecomposition of methyl orange in the liquid reaction was enhanced over the 2.0 mol% Si-incorporated TiO2 compared with that over pure TiO2: Methyl orange at 10.0 ppm was completely decomposed after 100 min when 1.0 g of the 2.0 mol% Si-incorporated TiO2 was used. (C) 2008 The Korean Society of Industrial and Engineering Chemistry. Published by Elsevier B.V. All rights reserved.