Effect of stress ratios on tension-tension fatigue behavior and micro-damage evolution of basalt fiber-reinforced epoxy polymer composites
被引:29
作者:
Zhao, Xing
[1
]
Wang, Xin
[1
,2
]
Wu, Zhishen
[1
,2
]
Keller, Thomas
[3
]
Vassilopoulos, Anastasios P.
[3
]
机构:
[1] Southeast Univ, Int Inst Urban Syst Engn, Natl & Local Unified Engn Res Ctr Basalt Fiber Pr, Nanjing 210096, Jiangsu, Peoples R China
[2] Southeast Univ, Key Lab C&PC Struct, Minist Educ, Nanjing 210096, Jiangsu, Peoples R China
[3] Ecole Polytech Fed Lausanne, Composite Construct Lab CCLab, CH-1015 Lausanne, Switzerland
基金:
美国国家科学基金会;
关键词:
LIFE-PREDICTION;
STIFFNESS REDUCTION;
FRP;
MECHANISMS;
TENDONS;
DIAGRAMS;
D O I:
10.1007/s10853-018-2260-1
中图分类号:
T [工业技术];
学科分类号:
08 ;
摘要:
The tension-tension fatigue behavior and damage mechanism of basalt fiber-reinforced epoxy polymer (BFRP) composites at different stress ratios are studied in this paper. The fatigue experiments were performed under stress ratios, R = sigma (min)/sigma (max) of 0.1 and 0.5, while the lifetime and the stiffness degradation were monitored and analyzed to investigate the effect of stress ratios. The damage propagation during fatigue loading was periodically monitored by using an in situ scanning electron microscope (SEM). The results show that the fatigue life decreases and the fatigue life degradation rate increases with the decrease of stress ratio for examined BFRP composites. The stiffness degradation is also sensitive to different stress ratios, showing a greater stiffness loss before failure at lower stress ratio. From the SEM images, it is indicated that the micro-damage mode shifts from interface debonding and matrix cracking into fiber breaking with decreasing stress ratios.