High Li+ conduction in NASICON-type Li1+x,YxZr2-x(PO4)3 at room temperature

被引：76
作者：
Li, Yutao [1 ]
Liu, Meijing [1 ,2 ]
Liu, Kai [1 ]
Wang, Chang-An [1 ]
机构：
[1] Tsinghua Univ, State Key Lab New Ceram & Fine Proc, Sch Mat Sci & Engn, Beijing 100084, Peoples R China
[2] Jingdezhen Ceram Inst, Sch Mat Sci & Engn, Jingdezhen 333001, Jiangxi, Peoples R China
来源：
JOURNAL OF POWER SOURCES | 2013年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Li solid electrolyte; NASICON; Li-ion battery; Ionic conductivity; LITHIUM TITANIUM PHOSPHATE; IONIC-CONDUCTIVITY; NEUTRON-DIFFRACTION; SOLID ELECTROLYTES; ALPHA-LIZR2(PO4)(3); FRAMEWORK; BATTERIES; MOBILITY;
D O I：
10.1016/j.jpowsour.2013.03.175
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The NASICON oxides with general formula Li1-xYxZr2-x(PO4)(3) (0.1 <= x <= 0.2) are prepared by conventional solid-state reaction. The samples are characterized by XRD, SEM, electrochemical impedance spectroscopy and Li-7 MAS NMR measurements. The structures are refined by the Rietveld method from powder X-ray diffraction data. With the introduction of Y3+, the volume of the large M1 cavity is reduced and the rhombohedral NASICON phase is stabilized at room temperature. The bulk and total Li+ conductivities of Li(1.15)Y(0.15)Zi(1.85)(PO4)(3) sintered by SPS are 1.4 x 10(-4) and 0.71 x 10(-4) S cm(-1) at 25 degrees C, respectively; the activation energy is about 0.39 eV in the temperature range 300-473 K. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码：50 / 53
页数：4
相关论文
共 50 条
  • [41] NMR investigations of Li+ ion dynamics in the NASICON ionic conductors Li1-xLax/3□2x/3Zr2(PO4)3
    Barre, Maud
    Emery, Joel
    Florian, Pierre
    Le Berre, Francoise
    Crosnier-Lopez, Marie-Pierre
    Fourquet, Jean-Louis
    JOURNAL OF PHYSICS-CONDENSED MATTER, 2009, 21 (17)
  • [42] Ionic conductivity of NASICON-type LiHf2(PO4)(3): A reexamination
    MartinezJuarez, A
    Iglesias, JE
    Rojo, JM
    SOLID STATE IONICS, 1996, 91 (3-4) : 295 - 301
  • [43] Lithium location in NASICON-type Li+ conductors by neutron diffraction:: II.: Rhombohedral α-LiZr2(PO4)3 at T=423 K
    Catti, M
    Stramare, S
    SOLID STATE IONICS, 2000, 136 : 489 - 494
  • [44] Li-ion transport studies of NASICON-type LiZr2(PO4)3 solid electrolyte crystallizing in rhombohedral structure at room temperature
    Khatua, Sumit
    Rao, Y. Bhaskara
    Achary, K. Ramakrushna
    Patro, L. N.
    SURFACES AND INTERFACES, 2023, 41
  • [45] The Li+ conducting composite based on LiTi2(PO4)3 and Li3BO3 glass
    Kwatek, K.
    Swiniarski, M.
    Nowinski, J. L.
    JOURNAL OF SOLID STATE CHEMISTRY, 2018, 265 : 381 - 386
  • [46] Competition between activation energy and migration entropy in lithium ion conduction in superionic NASICON-type Li1-3xGaxZr2(PO4)3
    Duan, Shanshan
    Huang, Can
    Liu, Min
    Cao, Zhiwen
    Tian, Xiaocong
    Hou, Shuen
    Li, Jiangyu
    Huang, Boyuan
    Jin, Hongyun
    JOURNAL OF MATERIALS CHEMISTRY A, 2021, 9 (12) : 7817 - 7825
  • [47] The NASICON solid solution Li1-x La x /3Zr2(PO4)3: optimization of the sintering process and ionic conductivity measurements
    Barre, M.
    Le Berre, F.
    Crosnier-Lopez, M-P.
    Galven, C.
    Bohnke, O.
    Fourquet, J-L.
    IONICS, 2009, 15 (06) : 681 - 687
  • [48] Thin-Film NASICON-Type Li1+xAlxTi2-x(PO4)3 Solid Electrolyte Directly Fabricated on a Graphite Substrate with a Hydrothermal Method Based on Different Al Sources
    Peng, Cong
    Kamiike, Yuichiro
    Liang, Yanjie
    Kuroda, Kensuke
    Okido, Masazumi
    ACS SUSTAINABLE CHEMISTRY & ENGINEERING, 2019, 7 (12) : 10751 - 10762
  • [49] Preparation and characterization of sol-gel derived high lithium ion conductive NZP-type ceramics Li1+x AlxTi2-x(PO4)3
    Bucharsky, E. C.
    Schell, K. G.
    Hintennach, A.
    Hoffmann, M. J.
    SOLID STATE IONICS, 2015, 274 : 77 - 82
  • [50] A mixed α/β superstructure in NASICON ionic conductors:: Neutron diffraction study of Li2FeTi(PO4)3 and Li2FeZr(PO4)3
    Catti, M
    JOURNAL OF SOLID STATE CHEMISTRY, 2001, 156 (02) : 305 - 312
12345