Fatigue crack closure: From LCF to small scale yielding

被引：57

作者：

Pippan, R. ^{[1
]}

Grosinger, W. ^{[1
]}

机构：

[1] Austrian Acad Sci, Erich Schmid Inst Mat Sci, A-8700 Leoben, Austria

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2013年 / 46卷

关键词：

Crack closure; Low cycle fatigue; Small scale yielding; Micro-cracks; Long cracks; WAKE PLASTICITY; PROPAGATION; THRESHOLD; RECONSIDERATION; OVERLOADS; DUCTILE; LENGTH; STRESS; GROWTH; ERROR;

D O I：

10.1016/j.ijfatigue.2012.02.016

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Most of the research on crack closure has been devoted to crack propagation under small scale yielding. In this paper, the effect of different length scale from micro-crack to long cracks and different loading conditions from low cycle fatigue, LCF, to small scale yielding on crack closure are considered. The main focus is on LCF crack closure behaviour which is studied by in situ fatigue experiments in a scanning electron microscope. The results demonstrate the importance of crack closure for the explanation of the LCF behaviour. The change of crack closure from LCF to high cycle fatigue and their consequences for lifetime prediction will be discussed. (C) 2012 Elsevier Ltd. All rights reserved.

引用

页码：41 / 48

页数：8

共 50 条

[31] New solution of near crack line field for an antiplane crack under small scale yielding
Yi, ZJ
Yang, DJ
Xiao, SX
Wang, SJ
Han, Y
INTERNATIONAL JOURNAL OF FRACTURE, 1997, 87 (04) : L119 - L123
[32] Small time scale fatigue crack growth analysis
Lu, Zizi
Liu, Yongming
INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (08) : 1306 - 1321
[33] A comparison of DIC-based techniques to measure crack closure in LCF
Patriarca, L.
Foletti, S.
Beretta, S.
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2018, 98 : 230 - 243
[34] Fatigue crack shielding and deflection in plain bearings under large-scale yielding
Burke-Veliz, A.
Syngellakis, S.
Reed, P. A. S.
ENGINEERING FAILURE ANALYSIS, 2010, 17 (03) : 648 - 657
[35] ON THE GEOMETRY OF FATIGUE CRACK CLOSURE
STUWE, HP
PIPPAN, R
SHAN, GX
STEEL RESEARCH, 1992, 63 (08): : 368 - 370
[36] RECONSIDERATION OF FATIGUE CRACK CLOSURE
VASUDEVAN, AK
SADANANDA, K
LOUAT, N
SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (11): : 1673 - 1678
[37] CRACK OPENING AND CLOSURE IN FATIGUE
SEHITOGLU, H
ENGINEERING FRACTURE MECHANICS, 1985, 21 (02) : 329 - 339
[38] A MODEL FOR FATIGUE CRACK CLOSURE
BEEVERS, CJ
BELL, K
CARLSON, RL
STARKE, EA
ENGINEERING FRACTURE MECHANICS, 1984, 19 (01) : 93 - &
[39] Relationship Between Closure Stress of Small Fatigue Crack and Ultrasonic Response
M. A. Salam Akanda
M. Saka
Journal of Nondestructive Evaluation, 2004, 23 : 37 - 47
[40] Microstructural effects on crack closure and propagation thresholds of small fatigue cracks
Akiniwa, Y
Tanaka, K
Kimura, H
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2001, 24 (12) : 817 - 829

← 1 2 3 4 5 →