Application of small punch creep testing to a thermally sprayed CoNiCrAlY bond coat

被引:52
作者
Chen, H. [1 ]
Hyde, T. H. [1 ]
Voisey, K. T. [1 ]
McCartney, D. G. [1 ]
机构
[1] Univ Nottingham, Fac Engn, Div Mat Mech & Struct, Nottingham NG7 2RD, England
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 585卷
关键词
HVOF thermal spraying; MCrAlY bond coat; Mechanical testing; Creep; Phase transformation; AFFECTING TGO GROWTH; MECHANICAL-PROPERTIES; SYSTEMS; BEHAVIOR; FRACTURE; ALLOY;
D O I
10.1016/j.msea.2013.06.080
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
High velocity oxy-fuel thermal spraying was used to prepare free-standing CoNiCrAlY (Co-31.7% Ni-20.8% Cr-8.1% Al-0.5% Y (wt%)) bond coat alloy samples approximately 0.5 mm thick. Creep tests were conducted at 750 degrees C on these samples using a small punch (SP) creep test method. The samples were characterised before and after creep testing using scanning electron microscopy with electron backscatter diffraction (EBSD). EBSD revealed a two phase fcc gamma-Ni and bcc B2 beta-NiAl microstructure with grain sizes similar to 1-2 mu m for both phases, which did not change significantly following testing. The constant temperature SP test data were characterised by a minimum creep strain rate, epsilon(min), and a total time to failure, t(f), at different applied stresses. The data are fitted to conventional power law equations with a stress exponent for creep close to 8 in the Norton power law and between 7 and 10 in the Monkman-Grant creep rupture law. Creep rupture was predominantly due to creep cavitation voids nucleating at both the gamma-beta interphase boundaries and the gamma-gamma grain boundaries leading to final failure by void linkage. However, rupture life was influenced by the quantity of oxide entrained in the coating during the spray deposition process. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码:205 / 213
页数:9
相关论文
共 34 条
[1]   Application of the CEN (European Committee for Standardization) small punch creep testing code of practice to a representative repair welded P91 pipe [J].
Blagoeva, D. T. ;
Hurst, R. C. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 510-11 :219-223
[2]  
Bose S., 2007, HIGH TEMPERATURE COA
[3]  
CEN, 2006, 156272006E CWA CEN
[5]   Monkman-grant analysis of creep fracture in dispersion-strengthened and particulate-reinforced aluminum [J].
Dunand, DC ;
Han, BQ ;
Jansen, AM .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (03) :829-838
[6]   Mechanisms controlling the durability of thermal barrier coatings [J].
Evans, AG ;
Mumm, DR ;
Hutchinson, JW ;
Meier, GH ;
Pettit, FS .
PROGRESS IN MATERIALS SCIENCE, 2001, 46 (05) :505-553
[7]   Technical and economical aspects of current thermal barrier coating systems for gas turbine engines by thermal spray and EBPVD: A review [J].
Feuerstein, Albert ;
Knapp, James ;
Taylor, Thomas ;
Ashary, Adil ;
Bolcavage, Ann ;
Hitchman, Neil .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2008, 17 (02) :199-213
[8]   Failure in notched tension bars due to high-temperature creep: Interaction between nucleation controlled cavity growth and continuum cavity growth [J].
Hayhurst, D. R. ;
Lin, J. ;
Hayhurst, R. J. .
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2008, 45 (7-8) :2233-2250
[9]   STRESS RUPTURE AND CREEP-BEHAVIOR OF A LOW-PRESSURE PLASMA-SPRAYED NICOCRALY COATING ALLOY IN AIR AND VACUUM [J].
HEBSUR, MG ;
MINER, RV .
THIN SOLID FILMS, 1987, 147 (02) :143-152
[10]   HIGH-TEMPERATURE TENSILE AND CREEP-BEHAVIOR OF LOW-PRESSURE PLASMA-SPRAYED NI-CO-CR-AL-Y COATING ALLOY [J].
HEBSUR, MG ;
MINER, RV .
MATERIALS SCIENCE AND ENGINEERING, 1986, 83 (02) :239-245