Low cycle fatigue of Eurofer 97

被引:96
作者
Marmy, Pierre [1 ]
Kruml, Tomas [2 ]
机构
[1] Ecole Polytech Fed Lausanne, Ctr Rech Phys Plasmas, CH-5232 Villigen, Switzerland
[2] Inst Phys Mat, Brno 61262, Czech Republic
关键词
D O I
10.1016/j.jnucmat.2008.02.054
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
We have investigated the low cycle fatigue and creep-fatigue properties of Eurofer 97 and observed the associated microstructural changes. The as received structure is composed of equiaxed subgrains and a few martensite laths with a high dislocation density. Fatigue tests have been carried out in air or in high vacuum, from room temperature to 550 degrees C, under total strain control. It has been found that the influence of the test temperature on the fatigue endurance is not significant. The softening behaviour as a function of the imposed strain amplitude and temperature has been analysed in detail. The softening rate is independent of the imposed strain but strongly enhanced at the highest test temperature. Creep-fatigue tests were run, imposing a 500 s dwell at the maximum tensile strain of the loading cycle, at a total strain range of 0.5%, 0.8% and 1.4%, and at 150, 300 and 550 degrees C. The influence of the hold time is important only at the highest test temperature, under low applied strains. It was found that at the beginning of life, at the highest temperature, the softening rate with hold times is much stronger as compared to the softening rate without hold times. The amount of stress relaxed during the dwell is independent of the applied strain, at the end of life. The effect of fatigue with and without hold times up to medium temperatures on the microstructure was to lower the dislocation density and to decompose the laths and large grains into a homogeneous structure of submicron grains. At the highest test temperature, an increase of the subgrain size and carbide coarsening were observed. (c) 2008 Elsevier B.V. All rights reserved.
引用
收藏
页码:52 / 58
页数:7
相关论文
共 8 条
[1]   High temperature deformation and damage behavior of RAFM steels under low cycle fatigue loading: Experiments and modeling [J].
Aktaa, J. ;
Schmitt, R. .
FUSION ENGINEERING AND DESIGN, 2006, 81 (19) :2221-2231
[2]   Cyclic instability of martensite laths in reduced activation ferritic/martensitic steels [J].
Armas, AF ;
Petersen, C ;
Schmitt, R ;
Avalos, M ;
Alvarez, I .
JOURNAL OF NUCLEAR MATERIALS, 2004, 329 :252-256
[3]  
Coffin L.F., 1954, T AM SOC MECH ENG, V76, P931, DOI [10.1115/1.4015020, DOI 10.1115/1.4015020]
[4]   INVESTIGATION OF MICROSTRUCTURAL CHANGES IN A FERRITIC STEEL CAUSED BY HIGH-TEMPERATURE FATIGUE [J].
KIM, S ;
WEERTMAN, JR .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (04) :999-1007
[5]  
MANSON SS, 1964, P 10 SAG ARM RES C S
[6]   Dislocation structures of duplex stainless steel in uniaxial and biaxial cyclic loading [J].
Petrenec, M ;
Aubin, V ;
Polák, J ;
Degallaix, S .
MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE IV, 2005, 482 :179-182
[7]   Cyclically induced softening due to low-angle boundary annihilation in a martensitic steel [J].
Sauzay, M ;
Brillet, H ;
Monnet, I ;
Mottot, M ;
Barcelo, F ;
Fournier, B ;
Pineau, A .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 400 :241-244
[8]  
VICTORIA M, 1995, ASTM STP, V1270