Effects of C layer on the microstructure and magnetic properties of FePt recording media films

被引：1
|
作者：
Zhen, CM [1 ]
Zhai, XX [1 ]
Ma, L [1 ]
Li, ML [1 ]
Nie, XF [1 ]
机构：
[1] Hebei Normal Univ, Inst Phys, Shandong 050016, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY | 2006年 / 129卷 / 1-3期
基金：
中国国家自然科学基金;
关键词：
magnetron sputtering system; mutilayer films; magnetic recording material; hysteresis loops;
D O I：
10.1016/j.mseb.2005.07.020
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
FePt/C mutilayer films were fabricated by magnetron sputtering system, then postannealed in vacuum. X-ray diffraction measurements show that the as-deposited films were disordered and the ordered L-10 structure was obtained by annealing the film at 600 degrees C with the c/a ratio 0.968. Magnetic investigation indicated that [FePt (2.5 nm)/C (2.0 nm)](10) film has the optimal magnetic properties with coercivity of 3245.1 Oe. By annealing the [FePt (2.5 nm)/C (2.0 nm)](10) film at 600 degrees C, magnetic particles with the size of about 10 nm dispersed uniformly in nonmagnetic C matrix was observed by an atomic force microscopy. (c) 2005 Elsevier B.V. All rights reserved.
引用
收藏
页码：261 / 264
页数：4
相关论文
共 50 条
  • [41] Effect of TiN-ZrO2 intermediate layer on the microstructure and magnetic properties of FePt and FePt-SiO2-C thin films
    Dong, K. F.
    Mo, W. Q.
    Jin, F.
    Song, J. L.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2017, 432 : 323 - 329
  • [42] Effect of FePt-C nucleation layer on magnetic properties and nanostructure for FePt-C/FePt-oxide stacked media
    Timm, Kim Kong
    Saito, Takashi
    Kushibiki, Ryosuke
    Saito, Shin
    2021 IEEE INTERNATIONAL MAGNETIC CONFERENCE (INTERMAG), 2021,
  • [43] Magnetic and structural properties of FePt-FeRh exchange spring films for thermally assisted magnetic recording media
    Thiele, JU
    Maat, S
    Robertson, JL
    Fullerton, EE
    IEEE TRANSACTIONS ON MAGNETICS, 2004, 40 (04) : 2537 - 2542
  • [44] Magnetization reversal and microstructure of FePt-Ag (001) particulate thin films for perpendicular magnetic recording media
    Wei, D. H.
    Yuan, F. T.
    Chang, H. W.
    You, K. L.
    Liou, Y.
    Yao, Y. D.
    Wu, J. K.
    JOURNAL OF APPLIED PHYSICS, 2008, 103 (07)
  • [45] Microstructure and magnetic properties of FePt and Fe/FePt polycrystalline films with high coercivity
    Takahashi, YK
    Seki, TO
    Hono, K
    Shima, T
    Takanashi, K
    JOURNAL OF APPLIED PHYSICS, 2004, 96 (01) : 475 - 481
  • [46] Effect of Pt and FePt Layer Thickness on Microstructure and Magnetic Properties of L10 FePt Films With Perpendicular Anisotropy
    Bae, Jee-Hwan
    Kim, Tae Kyoung
    Kim, Hyeon Min
    Hong, Jae-Young
    Kim, Ji-Young
    Cho, Min Kyung
    Kim, Gyeung Ho
    Ha, Heon-Young
    Chun, Dong Won
    IEEE TRANSACTIONS ON MAGNETICS, 2019, 55 (08)
  • [47] Effects of Ag Layer on the Structure and Magnetic Properties of FePt:AlN Composite Films
    Liu, Wenfeng
    Chai, Yuesheng
    Sun, Gang
    Zhang, Mingang
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2009, 25 (06) : 795 - 798
  • [48] Influence of Intermediate Layer on Magnetic Properties of L10 Ordered FePt Perpendicular Recording Media
    Li, Xu
    Li, Zhenghua
    Liu, Xi
    Li, Yanbo
    Bai, Jianmin
    Wei, Fulin
    Wei, Dan
    IEEE TRANSACTIONS ON MAGNETICS, 2010, 46 (06) : 2024 - 2027
  • [49] Magnetic properties of soft layer/FePt-MgO exchange coupled composite perpendicular recording media
    阴津华
    Takao Suzuki
    潘礼庆
    Chinese Physics B, 2008, (10) : 3907 - 3909
  • [50] Effects of composition and temperature of crystallization on the microstructure and magnetic properties of NdFeB thin films for perpendicular recording media
    Ma, YG
    Yang, Z
    Matsumoto, M
    Morisako, A
    Takei, S
    PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2003, 199 (03): : 491 - 500
12345