Effects of C layer on the microstructure and magnetic properties of FePt recording media films

被引：1
|
作者：
Zhen, CM [1 ]
Zhai, XX [1 ]
Ma, L [1 ]
Li, ML [1 ]
Nie, XF [1 ]
机构：
[1] Hebei Normal Univ, Inst Phys, Shandong 050016, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY | 2006年 / 129卷 / 1-3期
基金：
中国国家自然科学基金;
关键词：
magnetron sputtering system; mutilayer films; magnetic recording material; hysteresis loops;
D O I：
10.1016/j.mseb.2005.07.020
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
FePt/C mutilayer films were fabricated by magnetron sputtering system, then postannealed in vacuum. X-ray diffraction measurements show that the as-deposited films were disordered and the ordered L-10 structure was obtained by annealing the film at 600 degrees C with the c/a ratio 0.968. Magnetic investigation indicated that [FePt (2.5 nm)/C (2.0 nm)](10) film has the optimal magnetic properties with coercivity of 3245.1 Oe. By annealing the [FePt (2.5 nm)/C (2.0 nm)](10) film at 600 degrees C, magnetic particles with the size of about 10 nm dispersed uniformly in nonmagnetic C matrix was observed by an atomic force microscopy. (c) 2005 Elsevier B.V. All rights reserved.
引用
收藏
页码：261 / 264
页数：4
相关论文
共 50 条
  • [1] Capping C layer effects on magnetic properties and microstructure of FePt/MoC/CrRu films.
    Tsai, J.
    Fu, S.
    Tseng, Y.
    Li, C.
    2015 IEEE MAGNETICS CONFERENCE (INTERMAG), 2015,
  • [2] Effects of Substrate Bias With Recording Layer on the Magnetic Properties and Microstructure of Perpendicular Magnetic Recording Media
    Shi, J. Z.
    Lim, W. K.
    Phyoe, W. L.
    Hu, J. F.
    Cher, K. M.
    Zhou, T. J.
    Yang, Y.
    IEEE TRANSACTIONS ON MAGNETICS, 2013, 49 (06) : 2682 - 2685
  • [3] Fabrication of FePt films for magnetic recording media
    Wei, Fulin
    Yang, Zheng
    IEICE TRANSACTIONS ON ELECTRONICS, 2007, E90C (08): : 1570 - 1576
  • [4] Effect of capped layer on microstructure and magnetic properties of FePt films
    Chen, S. C.
    Kuo, P. C.
    Shen, C. L.
    Lin, G. P.
    Huang, K. T.
    Ou, S. L.
    Hong, W. H.
    MATERIALS & DESIGN, 2010, 31 (04) : 1742 - 1745
  • [5] Magnetic Properties and Microstructure of FePt Films With MgTiON Intermediate Layer
    Tsai, Jai Lin
    Li, Hsu Kang
    Pan, Zu Yu
    Chang, Yuan Shuo
    Chen, Yu Ren
    Pi, Chen
    Wu, Yu Ting
    Chang, Ching Wei
    IEEE TRANSACTIONS ON MAGNETICS, 2017, 53 (11)
  • [6] Microstructure and magnetic properties of FePt-TiC-C granular thin films for perpendicular recording
    Cui, W. B.
    Varaprasad, B. S. D. Ch. S.
    Takahashi, Y. K.
    Shiroyama, T.
    Hono, K.
    SOLID STATE COMMUNICATIONS, 2014, 182 : 17 - 21
  • [7] Microstructure and magnetic properties of granular FePt/(FePt)27Ti73 films for ultrahigh-density recording media
    Yu, HY
    Sun, HY
    Feng, SZ
    Gao, FJ
    Zhou, HJ
    Nie, XF
    Sun, YP
    JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2005, 12 (02): : 155 - 158
  • [8] Effects of CrRu underlayer and CrRu capped layer on the microstructure and magnetic properties of FePt films
    Chen, S. C.
    Kuo, P. C.
    Lee, C. T.
    Sun, A. C.
    Chou, C. Y.
    Fang, Y. H.
    IEEE TRANSACTIONS ON MAGNETICS, 2007, 43 (02) : 876 - 878
  • [9] Effects of B4C Addition on the Microstructure and Magnetic Properties of FePt-C Granular Thin Films for Perpendicular Magnetic Recording
    Yu, Dedong
    Zhou, Xiaoqian
    Zhang, Tongbo
    Zhong, Hui
    Fu, Yanqing
    Cui, Weibin
    Wang, Qiang
    IEEE TRANSACTIONS ON MAGNETICS, 2017, 53 (08)
  • [10] Microstructure and magnetic properties of FePt-SiO2 perpendicular recording media
    Hu, J. F.
    Chen, J. S.
    Lim, B. C.
    Liu, B.
    PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2008, 205 (10): : 2458 - 2463
12345