Evolution Mechanism of Non-metallic Inclusions in Al-Killed Alloyed Steel during Secondary Refining Process

被引:160
作者
Deng, Zhiyin [1 ]
Zhu, Miaoyong [1 ]
机构
[1] Northeastern Univ, Sch Met & Mat, Shenyang 110819, Peoples R China
基金
高等学校博士学科点专项科研基金; 中国国家自然科学基金;
关键词
non-metallic inclusions; spinel; calcium aluminate; thermodynamic calculation; evolution mechanism; secondary refining; DEOXIDATION EQUILIBRIUM; FREE-ENERGIES; THERMODYNAMICS; CALCIUM; ALUMINUM;
D O I
10.2355/isijinternational.53.450
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The evolution mechanism of inclusions in Al-killed alloyed steel during secondary refining process was studied by industrial experiments and thermodynamic calculations. It is found that during the tapping process, Al-O deoxidization reaction is very close to equilibrium with the formation of many Al2O3 clusters. With the slag/steel reaction, inclusions vary with the route as Al2O3 inclusions -> MgO-Al2O3 system inclusions -> CaO-MgO-Al2O3 system inclusions, and finally change into globular inclusions surrounded by CaO-Al2O3 outer layer, of which the melting point is lower than liquid steel temperature. Since MgO is less stable than CaO and it is easier to be reduced by Al, dissolved Mg is generated earlier and faster than Ca before LF refining, thus the MgO-Al2O3 system inclusions form at first. The mapping photos of inclusions show that the evolution mechanism of MgO-Al2O3 system inclusions into CaO-MgO-Al2O3 system inclusions is Ca element substitution for Mg element in MgO-Al2O3 inclusions. The line scanning shows that there is also the reaction of Ca element substitution for Al element in the outer CaO-Al2O3 layer without MgO.
引用
收藏
页码:450 / 458
页数:9
相关论文
共 36 条
[1]  
[Anonymous], 1984, REC VAL EQ CONST REA, P255
[2]   Ladle glaze: major source of oxide inclusions during ladle treatment of steel [J].
Beskow, K ;
Sichen, D .
IRONMAKING & STEELMAKING, 2004, 31 (05) :393-400
[3]  
Custer C. C., 1985, ELECT FURNACE STEELM, P303
[4]   Activities of the constituents in spinel solid solution and free energies of formation of MgO, MgO •Al2O3 [J].
Fujii, K ;
Nagasaka, T ;
Hino, M .
ISIJ INTERNATIONAL, 2000, 40 (11) :1059-1066
[5]  
Han Q., 1990, P 6 INT IRON STEEL C, V1, P166
[6]   Shape control of alumina inclusions by double calcium addition treatment [J].
Ito, Yo-Ichi ;
Nara, Seikoh ;
Kato, Yoshiei ;
Suda, Mamoru .
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2007, 93 (05) :355-361
[7]   Deoxidation equilibrium of calcium in liquid iron [J].
Itoh, H ;
Hino, M ;
BanYa, S .
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1997, 83 (11) :695-700
[8]  
Itoh H, 1998, TETSU TO HAGANE, V84, P85
[9]  
Itoh H, 1997, TETSU TO HAGANE, V83, P773
[10]   Thermodynamics on the formation of spinel nonmetallic inclusion in liquid steel [J].
Itoh, H ;
Hino, M ;
BanYa, S .
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1997, 28 (05) :953-956