Hydrogen-enhanced fatigue crack growth in a single-edge notched tensile specimen under in-situ hydrogen charging inside an environmental scanning electron microscope

被引:63
作者
Wan, Di [1 ]
Deng, Yun [1 ]
Meling, Jan Inge Hammer [1 ]
Alvaro, Antonio [2 ]
Barnoush, Afrooz [1 ]
机构
[1] Norwegian Univ Sci & Technol, Dept Mech & Ind Engn, Richard Birkelands Vei 2B, N-7491 Trondheim, Norway
[2] SINTEF Ind, N-7456 Trondheim, Norway
关键词
Fatigue crack growth (FCG); Hydrogen embrittlement; SENT specimen; EBSD; SEM; PHASE-TRANSFORMATIONS; ASSISTED CRACKING; EMBRITTLEMENT; DISLOCATION; PROPAGATION; MECHANISM; FRACTURE; DEFORMATION; PLASTICITY; DIFFUSION;
D O I
10.1016/j.actamat.2019.03.032
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Fatigue crack growth (FCG) test was done on a pre-cracked single-edge notched tensile (SENT) specimen with oligocrystalline ferritic structure. Innovative in-situ hydrogen (H)- charging by plasma inside an environmental scanning electron microscope (ESEM) was adopted to directly observe the H influence on the FCG behavior of this material. Diverse in-situ and post-mortem characterization methods including secondary electron imaging, backscatter electron imaging, electron backscatter diffraction (EBSD) and scanning probe microscopy (SPM) were used to investigate the material's behavior. It was observed that the crack growth rate was enhanced by about one magnitude when H was charged, in comparison with the reference test in vacuum (Vac). The FCG procedure was concluded as strongly associated with the plasticity evolution in the vicinity of the crack-tip. A simple model based on the restricted plasticity was proposed for the H-enhanced FCG behavior. A peculiar frequency dependency of the H-enhanced FCG behavior was observed at low loading frequencies (0,015 Hz-0.15 Hz): under the same in-situ H-charging condition, a lower frequency gave a slower crack growth rate and vice versa. This behavior was explained by the thermally activated dislocation motion correlated with the plasticity shielding effect during crack growth. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:87 / 99
页数:13
相关论文
共 60 条
[1]  
Anderson T., 2005, FRACTURE MECHANICS F
[2]  
Beacham C. D., 1972, METALL MATER TRANS B, V3, P441, DOI DOI 10.1007/BF02642048
[3]   Interpretation of hydrogen-assisted fatigue crack propagation in BCC iron based on dislocation structure evolution around the crack wake [J].
Birenis, Domas ;
Ogawa, Yuhei ;
Matsunaga, Hisao ;
Takakuwa, Osamu ;
Yamabe, Junichiro ;
Prytz, Oystein ;
Thogersen, Annett .
ACTA MATERIALIA, 2018, 156 :245-253
[4]   HYDROGEN-ENHANCED LOCALIZED PLASTICITY - A MECHANISM FOR HYDROGEN-RELATED FRACTURE [J].
BIRNBAUM, HK ;
SOFRONIS, P .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 176 (1-2) :191-202
[5]   MECHANICAL-PROPERTIES OF METAL-HYDRIDES [J].
BIRNBAUM, HK .
JOURNAL OF THE LESS-COMMON METALS, 1984, 104 (01) :31-41
[6]   ON THE DETERMINATION OF THE HYDROGEN FUGACITY IN AN ENVIRONMENTAL CELL TEM FACILITY [J].
BOND, GM ;
ROBERTSON, IM ;
BIRNBAUM, HK .
SCRIPTA METALLURGICA, 1986, 20 (05) :653-658
[7]   Origin of Plasticity Length-Scale Effects in Fracture [J].
Chakravarthy, Srinath S. ;
Curtin, William A. .
PHYSICAL REVIEW LETTERS, 2010, 105 (11)
[8]   Hydrogen embrittlement revealed via novel in situ fracture experiments using notched micro-cantilever specimens [J].
Deng, Yun ;
Barnoush, Afrooz .
ACTA MATERIALIA, 2018, 142 :236-247
[9]  
Gangloff R.P., 2008, Environment-Induced Cracking of Materials, P141
[10]  
Gerberich W.W., 1996, Hydrogen Effects in Materials, 5th Proceedings of the International Conference on the Effect of Hydrogen on the Behavior of Materials, P539