Study of Processing Map and Effect of Hot Rolling on Mechanical Properties of Aluminum 5083 Alloy

被引:10
作者
Rudra, Amitava [1 ,2 ]
Ashiq, Mohammad [1 ,2 ]
Tiwari, Jitendar Kumar [1 ,2 ]
Das, Satyabrata [3 ]
Dasgupta, Rupa [3 ]
机构
[1] Acad Sci & Innovat Res AcSIR, Bhopal 462026, India
[2] CSIR Adv Mat & Proc Res Inst, Bhopal 462026, India
[3] Ex CSIR Adv Mat & Proc Res Inst, Bhopal 462026, India
关键词
Hot deformation; Aluminum; Activation energy; Processing map; Rolling; Mechanical property; MG (5083)/AL(2)O(3)P COMPOSITES; MICROSTRUCTURAL EVOLUTION; DEFORMATION-BEHAVIOR; DYNAMIC RECRYSTALLIZATION; TENSILE PROPERTIES; TEMPERATURE; TEXTURE; (5083)/SICP; PARTICLES; WORKING;
D O I
10.1007/s12666-020-02003-w
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Hot deformation behavior of aluminum 5083 alloy was studied based on the compression test done up to true strain 0.5 in the temperature range of 473-773 K and strain rate range of 0.01-10 s(-1). The Arrhenius equations were used to evaluate the average activation energy for deformation. Processing map was developed to identify the optimum, safe and unsafe zones for processing based on the compression data. Electron backscattered diffraction (EBSD) and scanning electron microscopy images revealed the underlying micro-mechanisms at various deformation conditions. Varying fraction of dynamic recrystallization was found to coexist with dynamic recovery at high deformation temperature and different strain rates. Based on the safe deformation zone, hot rolling was attempted and up to 80% reduction of initial thickness was achieved. EBSD analysis showed that the percentage of dynamically recrystallized grains increased with increment in rolling reduction. Progressive and substantial increment in yield strength, ultimate tensile strength, ductility and bulk hardness was achieved with increment in rolling reductions.
引用
收藏
页码:1809 / 1826
页数:18
相关论文
共 46 条
  • [11] Harris JN, 2014, MECH WORKING METALS, P144
  • [12] Honeycombe R.W.K., 1968, The Plastic Deformation of Metals
  • [13] Hot deformation mechanisms and microstructure evolution of SiCp/2014Al composite
    Huang, Zhiye
    Zhang, Xingxing
    Xiao, Bolyu
    Ma, Zongyi
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 722 : 145 - 157
  • [14] Humphreys F.J., 2012, Recrystallization and related annealing phenomena
  • [15] NUCLEATION OF RECRYSTALLIZATION AT 2ND PHASE PARTICLES IN DEFORMED ALUMINUM
    HUMPHREYS, FJ
    [J]. ACTA METALLURGICA, 1977, 25 (11): : 1323 - 1344
  • [16] Superplastic behavior of an Al-Mg alloy at elevated temperatures
    Kaibyshev, R
    Musin, F
    Lesuer, DR
    Nieh, TG
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 342 (1-2): : 169 - 177
  • [17] Hot deformation and processing map of 2519A aluminum alloy
    Li, H. Z.
    Wang, H. J.
    Liang, X. P.
    Liu, H. T.
    Liu, Y.
    Zhang, X. M.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (03): : 1548 - 1552
  • [18] Microstructure, texture and mechanical properties of continuous cast AA 5083 aluminium alloy
    Li, J.
    Zeng, Q.
    Wen, X. Y.
    Zhai, T.
    [J]. MATERIALS SCIENCE AND TECHNOLOGY, 2007, 23 (02) : 225 - 228
  • [19] Comparison of recrystallization texture in cold-rolled continuous cast AA5083 and 5182 aluminum alloys
    Li, J
    Liu, WC
    Zhai, T
    Kenik, EA
    [J]. SCRIPTA MATERIALIA, 2005, 52 (03) : 163 - 168
  • [20] Prediction of 42CrMo steel flow stress at high temperature and strain rate
    Lin, Y. C.
    Chen, Ming-Song
    Zhong, Jue
    [J]. MECHANICS RESEARCH COMMUNICATIONS, 2008, 35 (03) : 142 - 150