Dielectric and polarization behaviour of cellulose electro-active paper (EAPap)

Dielectric and polarization behaviour of electro-active paper (EAPap) were studied to understand the detailed material behaviour of EAPap as a novel smart material. It was revealed that the dielectric constant of EAPap was temperature and frequency dependent. The largest change in the dielectric constant was observed near 0 degrees C while the highest dielectric constant was obtained at around 100 degrees C, which might be related to the dipolar behaviour of the hydroxyl structure of cellulose and adsorbed or existing internal water molecules in cellulose EAPap. By thermal stimulated current measurement for polarization behaviour of cellulose EAPap, it was shown that the maximum current was observed in the temperature range 105-110 degrees C. Compared with the polarization behaviour in the low temperature range, abnormal polarization was observed under an applied field mainly due to the trapped space charge in EAPap, which indicates that cellulose EAPap has a similar material behaviour to that of electret polymers.