Hydrogen embrittlement and rock bolt stress corrosion cracking

被引：71

作者：

Villalba, Ernesto ^{[1
]}

Atrens, Andrej ^{[1
,2
]}

机构：

[1] Univ Queensland, Sch Engn, Div Mat, Brisbane, Qld 4072, Australia

[2] Swiss Fed Labs Mat Sci & Technol, EMPA, Dept 136, CH-8600 Dubendorf, Switzerland

来源：

ENGINEERING FAILURE ANALYSIS | 2009年 / 16卷 / 01期

关键词：

Stress corrossion cracking; Hydrogen embrittlement; Rock bolt; Steel; X65 PIPELINE STEEL; GRAIN-BOUNDARY; SCC; INITIATION; MICROSTRUCTURE; MICROANALYSIS; DIFFUSION; IRON; X52;

D O I：

10.1016/j.engfailanal.2008.01.004

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This paper considers our recent research on rock bolt stress corrosion cracking (SCC) which studied the influence of metallurgy using a range of (1) existing rock bolt steels and (2) commercial steels. The chemical composition, mechanical properties and microstructures of these steels varied considerably. The aim is to understand this failure mechanism and in particular to apply the knowledge gained from the study of SCC and hydrogen embrittlement (HE) of steels. The resistance of 1008, X65, X70 and 4145H to SCC/HE was similar, an effect which could be hardly expected as these steels have different strengths, microstructures and H-trap distributions. Different steel microstructures (pearlitic-ferritic and tempered martensite) had similar resistance to SCC and HE in the most aggressive conditions (pH 2.1 and - 1500 mV(SCE)) and had the same dimple rupture fracture surface. (c) 2008 Elsevier Ltd. All rights reserved.

引用

页码：164 / 175

页数：12

共 50 条

[21] Stress corrosion cracking fracture mechanisms in rock bolts
Gamboa, E
Atrens, A
JOURNAL OF MATERIALS SCIENCE, 2003, 38 (18) : 3813 - 3829
[22] Stress corrosion cracking fracture mechanisms in rock bolts
E. Gamboa
A. Atrens
Journal of Materials Science, 2003, 38 : 3813 - 3829
[23] Electrochemical characteristics of Al-Mg alloy in seawater for leisure ship: Stress corrosion cracking and hydrogen embrittlement
Kim, Seong-Jong
Han, Min-Su
Jang, Seok-Ki
KOREAN JOURNAL OF CHEMICAL ENGINEERING, 2009, 26 (01) : 250 - 257
[24] Material influence on the stress corrosion cracking of rock bolts
Gamboa, E
Atrens, A
ENGINEERING FAILURE ANALYSIS, 2005, 12 (02) : 201 - 235
[25] A generalised, multi-phase-field theory for dissolution-driven stress corrosion cracking and hydrogen embrittlement
Cui, Chuanjie
Ma, Rujin
Martinez-Paneda, Emilio
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2022, 166
[26] The role of hydrogen in microbiologically influenced corrosion and stress corrosion cracking
Biezma, MV
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2001, 26 (05) : 515 - 520
[27] On the stress corrosion cracking and hydrogen embrittlement of sensitized austenitic stainless steels in boiling saturated magnesium chloride solutions: Effect of applied stress
Alyousif, Osama M.
Nishimura, Rokuro
CORROSION SCIENCE, 2008, 50 (10) : 2919 - 2926
[28] Investigation of the hydrogen embrittlement susceptibility of T24 boiler tubing in the context of stress corrosion cracking of its welds
De Bruycker, Evy
Huysmans, Staf
Vanderlinden, Frederic
ECF22 - LOADING AND ENVIRONMENTAL EFFECTS ON STRUCTURAL INTEGRITY, 2018, 13 : 226 - 231
[29] Modeling Damage of the Hydrogen Enhanced Localized Plasticity in Stress Corrosion Cracking
Benbelaid, S.
Belouchrani, M. A.
Assoul, Y.
Bezzazi, B.
INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2011, 20 (06) : 831 - 844
[30] Rock bolt corrosion - an experimental study
Aziz, N.
Craig, P.
Nemcik, J.
Hai, F.
TRANSACTIONS OF THE INSTITUTIONS OF MINING AND METALLURGY SECTION A-MINING TECHNOLOGY, 2014, 123 (02): : 69 - 77

← 1 2 3 4 5 →