Influence of Nb-Ti composition on recrystallization of ferritic stainless steel

被引：0
作者：
Yang, Yiqiao [1 ]
Liu, Y. D. [2 ]
机构：
[1] Northeastern Univ, Res Inst, Shenyang 110004, Peoples R China
[2] Northeastern Univ, Minist Educ, Key Lab Anisotropy and Texture Mat, Shenyang 110004, Peoples R China
来源：
TEXTURES OF MATERIALS, PTS 1 AND 2 | 2012年 / 702-703卷
关键词：
Nb-Ti; annealing; texture; EBSD; TEXTURE; SHEET;
D O I：
10.4028/www.scientific.net/MSF.702-703.619
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
An experimental study of the microstructural and texture evolution attending recrystallization of Nb-Ti stabilized ferritic stainless steel is presented. Two specimens with different Nb-Ti compositions, TCS345 and B4003, have been selected for comparison. The result shows that, after annealing at 750 degrees C for 5min, the major orientation in the TCS345 specimen locates at {111}< 112 >, microstructures presents an equiaxed grain morphology, whereas the texture in the B4003 is not typical recrystallization texture and remains weak, indicating recrystallization occur preferentially to the TCS345 sheet. And after continuous annealing at 850 degrees C for 5 min, the texture in TCS345 remains stronger than in the B4003, indicating that the additional amount of Nb-Ti acts to significantly hinder the recrystallization process.
引用
收藏
页码：619 / +
页数：2
相关论文
共 7 条
  • [1] Effect of intermediate annealing on texture, formability and ridging of 17%Cr ferritic stainless steel sheet
    Huh, MY
    Engler, O
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 308 (1-2): : 74 - 87
  • [2] Evolution of microstructure and texture associated with ridging in ferritic stainless steels
    Park, SH
    Kim, KY
    Lee, YD
    Park, CG
    [J]. TEXTURES OF MATERIALS, PTS 1 AND 2, 2002, 408-4 : 1335 - 1340
  • [3] Shin H J, 2003, J ACTA MAT, V51, P4264
  • [4] Recrystallization of stabilized ferritic stainless steel sheet
    Sinclair, CW
    Mithieux, JD
    Schmitt, JH
    Bréchet, Y
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (11): : 3205 - 3215
  • [5] Development of ferritic stainless steel sheets with excellent deep drawability by {111} recrystallization texture control
    Yazawa, Y
    Ozaki, Y
    Kato, Y
    Furukimi, O
    [J]. JSAE REVIEW, 2003, 24 (04): : 483 - 488
  • [6] Effect of chromium content on relationship between r-value and {111} recrystallization texture in ferritic steel
    Yazawa, Y
    Muraki, M
    Kato, Y
    Furukimi, O
    [J]. ISIJ INTERNATIONAL, 2003, 43 (10) : 1647 - 1651
  • [7] Yazawa Y, 1999, J KAWASAKI STEEL TEC, V40, P23
1