Microstructure and mechanical properties of two-phase Fe30Ni20Mn20Al30: part II mechanical properties

被引:1
作者
Wu, X. [1 ]
Baker, I. [1 ]
Wu, H. [1 ]
机构
[1] Dartmouth Coll, Thayer Sch Engn, Hanover, NH 03755 USA
关键词
TEMPERATURE; FRACTURE; TENSILE; PHASE; FLOW;
D O I
10.1007/s10853-013-7449-8
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This paper describes the mechanical properties of B2/L2(1) two-phase Fe30Ni20Mn20Al30 (at.%) in both the as-cast condition and after a 72 h anneal at 823 K. The temperature dependence of the compressive strength of Fe30Ni20Mn20Al30 showed three distinct regions: (1) brittle fracture at low temperature, (2) plastic flow with a rapid decline in yield strength from 1500 to 250 MPa from the brittle-to-ductile transition temperature (BDTT) to 873 K, and (3) a slight decrease in yield strength to similar to 150 MPa from 873 to 1073 K. Interestingly, the BDTT (573 K) exhibited by the coarser microstructure present in 72 h annealed material was lower than that of the as-cast alloy (623 K). Using both differential scanning calorimetry and in situ heating in a transmission electron microscope, an L2(1)-to-B2 transition was found at 750 +/- A 25 K. A mixture of intergranular fracture and transgranular cleavage was observed after room temperature compression while only cleavage was found at 673 K. All the specimens deformed extensively without fracture when tested at temperatures higher than 673 K. The strain rate had little effect on the strength at 573 K and a moderate effect at 873 K with a strain-rate sensitivity exponent value of 0.1.
引用
收藏
页码:6535 / 6541
页数:7
相关论文
共 34 条
  • [1] THE EFFECT OF TEMPERATURE AND FE-AL RATIO ON THE FLOW AND FRACTURE OF FEAL
    BAKER, I
    XIAO, H
    KLEIN, O
    NELSON, C
    WHITTENBERGER, JD
    [J]. ACTA METALLURGICA ET MATERIALIA, 1995, 43 (04): : 1723 - 1730
  • [2] A REVIEW OF THE MECHANICAL-PROPERTIES OF B2 COMPOUNDS
    BAKER, I
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 192 : 1 - 13
  • [3] Baker I., 2005, TMS Proceedings: Processing and Fabrication of Advanced Materials XIV With Frontiers in Materials Science 2005: Innovative Materials and Manufacturing Techniques, P237
  • [4] Baker I., 2005, Microscopy and Microanalysis, V11, P1864
  • [5] Microstructural evolution of spinodally formed Fe35Ni15Mn25Al25
    Baker, Ian
    Zheng, R. K.
    Saxey, David W.
    Kuwano, Satoko
    Wittmann, Markus W.
    Loudis, Johnathan A.
    Prasad, K. S.
    Liu, Zongwen
    Marceau, Ross
    Munroe, P. R.
    Ringer, Simon P.
    [J]. INTERMETALLICS, 2009, 17 (11) : 886 - 893
  • [6] CORRELATION OF DEFORMATION MECHANISMS WITH THE TENSILE AND COMPRESSIVE BEHAVIOR OF NIAL AND NIAL(ZR) INTERMETALLIC ALLOYS
    BOWMAN, RR
    NOEBE, RD
    RAJ, SV
    LOCCI, IE
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (05): : 1493 - 1508
  • [7] Dieter GE, 1984, MECH METALLURGY, P453
  • [8] ROOM-TEMPERATURE TENSILE DUCTILITY IN POLYCRYSTALLINE B2 NIAL
    HAHN, KH
    VEDULA, K
    [J]. SCRIPTA METALLURGICA, 1989, 23 (01): : 7 - 12
  • [9] Precipitation of L2(1)-type Ni2AlTi Phase in B2-type Intermetallic Compounds NiTi
    Han, Chang-Suk.
    [J]. KOREAN JOURNAL OF MATERIALS RESEARCH, 2007, 17 (08): : 420 - 424
  • [10] A new high-strength spinodal alloy
    Hanna, JA
    Baker, I
    Wittmann, MW
    Munroe, PR
    [J]. JOURNAL OF MATERIALS RESEARCH, 2005, 20 (04) : 791 - 795