Mechanical characterization of mechanically alloyed ultrafine-grained Ti5Si3+40 vol% γ-TiAl composites

被引:10
作者
Suryanarayana, C. [1 ]
Behn, Rainer [1 ,2 ]
Klassen, Thomas [1 ,3 ]
Bormann, Ruediger [1 ]
机构
[1] Helmholtz Zentrum Geesthach, Ctr Mat & Coastal Res GmbH, Inst Mat Res, D-21502 Geesthacht, Germany
[2] Hamburg Univ Technol, Dept Mat Sci & Technol, D-21073 Hamburg, Germany
[3] Univ Fed Armed Forces Hamburg, Helmut Schmidt Univ, Inst Mat Technol, D-22043 Hamburg, Germany
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 579卷
关键词
Titanium alloys; Mechanical alloying; Mechanical characterization; Electron microscopy; Superplasticity; LOW-TEMPERATURE SUPERPLASTICITY; TENSILE DUCTILITY; NANOCRYSTALLINE; SIZE; DEFORMATION; BEHAVIOR; COMPACTION; CERAMICS;
D O I
10.1016/j.msea.2013.04.092
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Ultrafine-grained ceramic-based composites of Ti-31.6Al-21.6Si (at%) consisting of 60 vol% of zeta-Ti5Si3 and 40 vol% of gamma-TiAl were produced by high-energy ball milling followed by hot isostatic pressing (HIP). Because of the cleanliness of the powder and full densification of the HIPed product, the mechanical behavior of the composite could be unambiguously related to the microstructure and chemistry. The starting microstructure after HIPing consisted of intermixed zeta-Ti5Si3 and gamma-TiAl phases of approximately equal grain size, the size ranging from about 300 nm to I pm depending on the HIP temperature. Hightemperature mechanical testing of this ultrafine-grained composite exhibited a strain-rate sensitivity of > 0.3. Further, the equiaxed microstructure was retained after mechanical testing, suggesting the possibility of achieving superplastic deformation. Consequently, tensile testing demonstrated elongations of about 150% at 950 degrees C and a strain rate of 4 x 10(-5) s(-1). Considering that the present alloy has the ceramic (suicide) phase as the matrix, this temperature at which superplastic deformation is observed is significantly lower than that reported for conventional coarse-grained ceramic materials. (C) 2013 Elsevier B.V. All rights reserved.
引用
收藏
页码:18 / 25
页数:8
相关论文
共 66 条
  • [1] [Anonymous], 1995, PULVERMET WISSENSCHA
  • [2] [Anonymous], NATURE
  • [3] [Anonymous], THESIS TU HAMBURG HA
  • [4] Microstructure and deformation of two-phase γ-titanium aluminides
    Appel, F
    Wagner, R
    [J]. MATERIALS SCIENCE & ENGINEERING R-REPORTS, 1998, 22 (05) : 187 - 268
  • [5] Overview no. 130 - Size effects in materials due to microstructural and dimensional constraints: A comparative review
    Arzt, E
    [J]. ACTA MATERIALIA, 1998, 46 (16) : 5611 - 5626
  • [6] DIFFUSION-ACCOMMODATED FLOW AND SUPERPLASTICITY
    ASHBY, MF
    VERRALL, RA
    [J]. ACTA METALLURGICA, 1973, 21 (02): : 149 - 163
  • [7] SUPERPLASTIC-LIKE BEHAVIOR AT HIGH-STRAIN RATES IN MECHANICALLY ALLOYED ALUMINUM
    BIELER, TR
    NIEH, TG
    WADSWORTH, J
    MUKHERJEE, AK
    [J]. SCRIPTA METALLURGICA, 1988, 22 (01): : 81 - 86
  • [8] Bohn R, 2001, POWDER MATERIALS: CURRENT RESEARCH AND INDUSTRIAL PRACTICES, P107
  • [9] NANOCRYSTALLINE INTERMETALLIC COMPOUNDS - AN APPROACH TO DUCTILITY
    BOHN, R
    HAUBOLD, T
    BIRRINGER, R
    GLEITER, H
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1991, 25 (04): : 811 - 816
  • [10] Mechanical behavior of submicron-grained γ-TiAl-based alloys at elevated temperatures
    Bohn, R
    Klassen, T
    Bormann, R
    [J]. INTERMETALLICS, 2001, 9 (07) : 559 - 569