Nitrided Amorphous Stainless Steel Coatings Deposited by Reactive Magnetron Sputtering from an Austenitic Stainless Steel Target

Stainless steel films were reactively magnetron sputtered in argon/nitrogen gas flow onto oxidized silicon wafers using austenitic AISI 316 stainless-steel targets. The deposited films of about 300 nm thickness were characterized by conversion electron Mossbauer spectroscopy, magneto-optical Kerr-effect, X-ray diffraction, Rutherford backscattering spectrometry, and resonant nuclear reaction analysis. These complementary methods were used for a detailed examination of the nitriding effects for the sputtered stainless-steel films. The formation of an amorphous and soft ferromagnetic phase in a wide range of the processing parameters was found. Further, the influence of postvacuum-annealing was examined by perturbed angular correlation to achieve a comprehensive understanding of the nitriding process and phase formation. The amorphous phase is not very stable and crystallization can be observed at 973 K.