Enhancement of green long lasting phosphorescence in CaSnO3:Tb3+ by addition of alkali ions

Long lasting phosphors of CaSnO3:Tb3+ added alkali ions (Li+, Na+, K+) were prepared by solid-state reaction. The phosphorescence of samples consists of a group of green emission lines originating from D-5(4)-> E-7(J) transitions of Tb3+. The afterglow spectra and concentration quenching behaviors of fluorescence were investigated in the Tb3+ mono-doped sample. The result shows the optimal doping concentration of Tb3+ is 0.3 mol%. In the co-doped samples, the doping concentrations of Tb3+ and alkali ions are both at 0.3 mol%. It is found from the afterglow decay curves that the introduction of alkali ions can prolong the phosphorescent lasting time and the sample of incorporating Na+ shows the best result. Tb3+ and alkali ions can substitute Ca2+ ions, acting as hole and electron traps, respectively. The thermoluminescence (TL) spectra are also investigated. The depths of traps for the mono- and co-doped samples are calculated to be 0.622, 0.541, 0.529 and 0.538 eV, respectively. Moreover, the possible mechanism of the green long lasting phosphorescence is proposed based on the experiment results. (C) 2012 Elsevier BY. All rights reserved.