Synthesis and Infrared Stealth Property of Ordered Mesoporous Carbon-Aluminum-Doped Zinc Oxide Composites

被引：11

作者：

Wang, Wei ^{[1
]}

Zhang, Linping ^{[1
]}

Liu, Ying ^{[1
]}

Xu, Hong ^{[1
]}

Zhong, Yi ^{[1
]}

Mao, Zhiping ^{[1
]}

机构：

[1] Donghua Univ, Minist Educ, Key Lab Sci & Technol Ecotext, Shanghai 201620, Peoples R China

来源：

INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH | 2013年 / 52卷 / 43期

关键词：

EMISSIVITY; FILMS; ABSORPTION; SILICA;

D O I：

10.1021/ie401827s

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Ordered mesoporous carbon aluminum-doped zinc oxide (C-AZO) composites were prepared by the solvent-evaporation induced self-assembly method (EISA). The mesoporous structure was evaluated by small-angle X-ray scattering (SAXS), transmission electron microscopy (TEM), and N-2 adsorption-desorption. The results showed that the composites had uniform pore size and high surface area. Textural characteristics of the nanocomposites were affected by the carbonization temperature. The specific area and pore volume increased upon increasing the calcination temperature, while the pore diameter decreased. The infrared emissivity value (8-14 mu m) of ordered mesoporous C-AZO was measured by an IR-2 Infrared Emissometer. The results showed that infrared emissivity was as low as 0.39, which exhibited outstanding performance of infrared stealth.

引用

页码：15066 / 15074

页数：9

共 37 条

[31] Structure and infrared emissivity of collagen/SiO2 composite [J].

Ye, Xiaoyun ;

Zhou, Yuming ;

Sun, Yanqing ;

Chen, Jing ;

Wang, Zhiqiang .

APPLIED SURFACE SCIENCE, 2008, 254 (18) :5975-5980

[32] Preparation of leafing Cu and its application in low infrared emissivity coatings [J].

Yu, Huijuan ;

Xu, Guoyue ;

Shen, Xingmei ;

Yan, Xiaoxing ;

Huang, Rong ;

Li, Fenglei .

JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 484 (1-2) :395-399

[33] Organosilane-assisted synthesis of ordered mesoporous poly(furfuryl alcohol) composites [J].

Zhai, Yunpu ;

Tu, Bo ;

Zhao, Dongyuan .

JOURNAL OF MATERIALS CHEMISTRY, 2009, 19 (01) :131-140

[34] Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores [J].

Zhao, DY ;

Feng, JL ;

Huo, QS ;

Melosh, N ;

Fredrickson, GH ;

Chmelka, BF ;

Stucky, GD .

SCIENCE, 1998, 279 (5350) :548-552

[35] Direct Incorporation of Magnetic Constituents within Ordered Mesoporous Carbon-Silica Nanocomposites for Highly Efficient Electromagnetic Wave Absorbers [J].

Zhou, Jianhua ;

He, Jianping ;

Li, Guoxian ;

Wang, Tao ;

Sun, Dun ;

Ding, Xiaochun ;

Zhao, Jianqing ;

Wu, Shichao .

JOURNAL OF PHYSICAL CHEMISTRY C, 2010, 114 (17) :7611-7617

[36] Preparation and infrared emissivity of ZnO: Al (AZO) thin films [J].

Zhu, Dongmei ;

Li, Kun ;

Luo, Fa ;

Zhou, Wancheng .

APPLIED SURFACE SCIENCE, 2009, 255 (12) :6145-6148

[37]

Zhu Y. A., 2006, MAT REV, V20, P319

← 1 2 3 4 →