Studies on failure behaviour of wire rope used in underground coal mines

被引：63

作者：

Singh, R. P. ^{[1
]}

Mallic, Mousumi ^{[1
]}

Verma, M. K. ^{[1
]}

机构：

[1] Cent Inst Min & Fuel Res, CSIR, Met Sect, MHM, Brawa Rd, Dhanbad 826015, Bihar, India

来源：

ENGINEERING FAILURE ANALYSIS | 2016年 / 70卷

关键词：

Wire rope failure; Types of failure in wire rope; Wire rope; Corrosion on wire rope;

D O I：

10.1016/j.engfailanal.2016.09.002

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Wire ropes operate at high stress levels and are almost invariably subject to fluctuating loads. The continuous degradation of wire rope affected with operative services will ultimately lead to failure. Study of the causes of failure of two wire ropes from two different Indian coal mines have been carried out and discussed here. The investigating parameters comprises of physical examination, wear & corrosion, lubrication, macro & micro-examination and chemical composition. The investigation revealed that the major cause of failure was due to excessive wear and corrosion resulted in high reduction in diameter ranging from 50%-90% and poor lubrication condition of wire rope. Micro-examination also revealed intergranular corrosion with cracks and pittings, uniform corrosion with pitting along the grain. Further elongated grain which was indicative of stress due to excessive corrosion with sudden impact resulted in its failure. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：290 / 304

页数：15