Phase and Texture Evolution of Ag/Ni Composite-Sheathed Bi-2223 Tapes with Different Thickness

The influence of green tape thickness on the Bi-2223 phase formation and texture evolution in Ag/Ni composite-sheathed tapes fabricated by the "powder-in-tube" technique has been studied. Microstructural observations by SEM as well as critical current density (J (c)) measurements at 77 K, 0 T have been performed to analyze the performance of the tapes. The results show an important influence of the green tape thickness on the critical current depending on the content and texture of Bi-2223 phase. The J (c) increases with decreasing thickness. Moreover, texture measured by omega scans shows that the texture of the Bi-2223 phase is significantly influenced by the thickness of the green tape after the first and final sintering processes. Alignment of Bi-2223 grains in the thin tapes is much better. Higher performance of Ag/Ni composite-sheathed Bi-2223 tapes can be obtained by controlling the thickness of the green tapes.