Optimal Process Parameters for 3D Printing of Porcelain Structures

被引：37

作者：

Miyanaji, Hadi ^{[1
]}

Zhang, Shanshan ^{[1
]}

Lassell, Austin ^{[1
]}

Zandinejad, Amir Ali ^{[2
]}

Yang, Li ^{[1
]}

机构：

[1] Univ Louisville, Louisville, KY 40292 USA

[2] Texas A&M Univ, Dallas, TX USA

来源：

44TH NORTH AMERICAN MANUFACTURING RESEARCH CONFERENCE, NAMRC 44 | 2016年 / 5卷

关键词：

3D printing; Binder jetting process; green parts; sintering; FABRICATION; ACCURACY; INK;

D O I：

10.1016/j.promfg.2016.08.074

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Dental porcelain material is a typical glass ceramic material that is widely used in dental restoration applications. However, there still exists limited knowledge about the fabrication of this type of materials using binder jetting additive manufacturing process. There are several important factors such as saturation level, power level, drying time as well as spread speed, which would potentially affect the accuracy and strength of the printed parts before and after sintering. Therefore, in this research an extensive experimental study was performed to obtain the optimal process parameters for the dental porcelain materials fabricated via ExOne binder jetting system. The results also provide general printing guidelines for the fabrication of glass ceramic materials.