High temperature erosion-oxidation of Cr3C2-NiCr thermal spray coatings under simulated turbine conditions

被引：115
作者：
Matthews, S. [1 ]
James, B. [2 ]
Hyland, M. [2 ]
机构：
[1] Massey Univ, Sch Engn & Adv Technol, Auckland, New Zealand
[2] Univ Auckland, Dept Chem & Mat Engn, Auckland, New Zealand
来源：
CORROSION SCIENCE | 2013年 / 70卷
关键词：
Metal matrix composites; Metal coatings; Erosion; SEM; High temperature corrosion; Internal oxidation; OXIDE SCALES; INTERNAL OXIDATION; CHROMIUM CARBIDES; BASE ALLOYS; CORROSION; BEHAVIOR; NICKEL; MECHANISMS; CARBON; MICROSTRUCTURE;
D O I：
10.1016/j.corsci.2013.01.030
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Most erosion-oxidation research has been directed at high erodent flux, low impact velocity conditions typical of fluidised bed conditions. Few works have investigated erosion-oxidation under high temperature, high impact velocity, and low erodent flux conditions found within turbines. This work addresses the gap in knowledge of the high temperature erosion-oxidation mechanism of Cr3C2-NiCr coatings under long-term simulated turbine conditions. The same generic mechanism was observed under erosion-affected-oxidation and oxidation-affected-erosion conditions. The carbide and Cr3C2-NiCr phase interface was preferentially oxidised. An internal oxidation front progressed into the coating in advance of the slower erosive mass loss front at the surface. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：203 / 211
页数：9
相关论文
共 74 条
  • [1] [Anonymous], 1992, MATER MANUF PROCESS
  • [2] [Anonymous], 1979, EROSION PREVENTION U
  • [3] Assessment of mechanically mixed layer developed during high temperature erosion of cermets
    Antonov, Maksim
    Hussainova, Irina
    Pirso, Juri
    Volobueva, Olga
    [J]. WEAR, 2007, 263 (7-12 SPEC. ISS.) : 878 - 886
  • [4] Berger LM, 1996, THERMAL SPRAY: PRACTICAL SOLUTIONS FOR ENGINEERING PROBLEMS, P89
  • [5] Berger Z, 1996, HIGH TEMP MATER PROC, V15, P179
  • [6] Experimental and thermodynamic study of nickel-based alloys containing chromium carbides, Part 11: Study of the sub-surface characteristics of Ni-30 wt% Cr-xC alloys oxidized at high temperature using thermodynamic calculations
    Berthod, P.
    [J]. CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2008, 32 (03): : 492 - 499
  • [7] Study of the behavior in oxidation at high temperature of Ni, Co and Fe-base alloys containing very high fractions of carbides
    Berthod, Patrice
    Lemoine, Pierric
    Aranda, Lionel
    [J]. HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 7, PTS 1 AND 2, 2008, 595-598 : 871 - 880
  • [8] Influence of chromium carbides on the high temperature oxidation behavior and on chromium diffusion in nickel-base alloys
    Berthod, Patrice
    [J]. OXIDATION OF METALS, 2007, 68 (1-2): : 77 - 96
  • [9] The behaviour of oxide scales on metals under erosion-corrosion at high temperature
    Birks, N
    Pettit, FS
    Peterson, B
    [J]. HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 4, PTS 1 AND 2, 1997, 251-2 : 475 - 482
  • [10] Birks N., 1983, INTRO HIGH TEMPERATU
12345678