The effect of nanosilica on mechanical, thermal and morphological properties of epoxy coating

In this study, nanosilica of very high specific surface area is used as reinforcing filler for preparing an epoxy-based nanocomposite coating. For appropriate dispersion of nanoparticles in the polymer matrix, ultrasound waves were applied after mechanical mixing. The resulting perfect dispersion of nanosilica particles in epoxy coating revealed by transmission electron microscopy ensured the transparency of the nanocomposite. Nanoindentation was used to determine some mechanical properties such as hardness and elastic modulus. The obtained results show 26 and 21% increases in hardness and elastic modulus, respectively for resin filled with 5% nanosilica compared to neat epoxy. DMA results show that the glass transition temperature of samples is increased with increasing silica nanoparticles. The result of TGA shows significant improvement of the thermal decomposition temperature of epoxy coating containing 5% nanosilica compared to neat epoxy. Scanning electron microscopy (SEM) micrographs of fractured surfaces show increased roughness with nanosilica addition. (c) 2012 Elsevier B.V. All rights reserved.