Thermo-mechano-oxidative behavior at the ply's scale: The effect of oxidation on transverse cracking in carbon-epoxy composites

被引：21
作者：
Daghia, F. [1 ]
Zhang, F. [1 ]
Cluzel, C. [1 ,2 ]
Ladeveze, P. [1 ]
机构：
[1] Univ Paris Saclay, CNRS, ENS Cachan, LMT Cachan, F-94235 Cachan, France
[2] IUT Evry Val dEssonne, Dept SGM, F-91025 Evry, France
来源：
COMPOSITE STRUCTURES | 2015年 / 134卷
关键词：
Environmental degradation; Transverse cracking; Experimental testing; Finite fracture mechanics; POLYMER-MATRIX COMPOSITES; CONTINUUM DAMAGE MODEL; LAMINATED COMPOSITES; CROSS-PLY; INDUCED SHRINKAGE; MESOMODEL; TEMPERATURE; VALIDATION; ILLUSTRATIONS; PROPAGATION;
D O I：
10.1016/j.compstruct.2015.08.103
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The use of polymer matrix composites at relatively high temperatures (150-300 degrees C) requires accounting for the oxidation of the polymer and its coupling with mechanical degradation. A vast body of literature investigates these phenomena at very small scales, from the chemistry of the polymer to the mechanical behavior at the fiber's scale. The aim of this work is to apprehend the effect of oxidation on the transverse composite properties directly at the ply's scale, and in particular to examine its effect on the evolution of transverse cracking during aging and mechanical loading. Experimental results demonstrated the appearance of a new cracking scenario with respect to unaged composites, and a model based on finite fracture mechanics enabled us to explore the competition between the two different mechanisms. This work is a first step towards a damage mesomodel which incorporates the effects of oxidation aging. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：602 / 612
页数：11
相关论文
共 33 条
[1]   On the validation of a damage mesomodel for laminated composites by means of open-hole tensile tests on quasi-isotropic laminates [J].
Abisset, E. ;
Daghia, F. ;
Ladeveze, P. .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2011, 42 (10) :1515-1524
[2]   Finite-Element displacement fields analysis from digital images: Application to portevin-le chatelier bands [J].
Besnard, G. ;
Hild, F. ;
Roux, S. .
EXPERIMENTAL MECHANICS, 2006, 46 (06) :789-803
[3]   Transverse ply cracking in cross-ply CFRP laminates - Initiation or propagation controlled? [J].
Boniface, L ;
Smith, PA ;
Bader, MG ;
Rezaifard, AH .
JOURNAL OF COMPOSITE MATERIALS, 1997, 31 (11) :1080-1112
[4]   Influence of laminate thickness on composite durability for long term utilisation at intermediate temperature (100-150 °C) [J].
Cinquin, Jacques ;
Medda, Bruno .
COMPOSITES SCIENCE AND TECHNOLOGY, 2009, 69 (09) :1432-1436
[5]   Interaction between cracking and oxidation in organic matrix composites [J].
Colin, X ;
Mavel, A ;
Marais, C ;
Verdu, J .
JOURNAL OF COMPOSITE MATERIALS, 2005, 39 (15) :1371-1389
[6]   Kinetic modelling of the stabilizing effect of carbon fibres on thermal ageing of thermoset matrix composites [J].
Colin, X ;
Marais, C ;
Verdu, J .
COMPOSITES SCIENCE AND TECHNOLOGY, 2005, 65 (01) :117-127
[7]   A new method for predicting the thermal oxidation of thermoset matrices - Application to an amine crosslinked epoxy [J].
Colin, X ;
Marais, C ;
Verdu, J .
POLYMER TESTING, 2001, 20 (07) :795-803
[8]  
Daghia F, 2014, ECCM16, P22
[9]  
Daghia F, 2013, JNC18 NANT
[10]   Identification and validation of an enhanced mesomodel for laminated composites within the WWFE-III [J].
Daghia, Federica ;
Ladeveze, Pierre .
JOURNAL OF COMPOSITE MATERIALS, 2013, 47 (20-21) :2675-2694
1234