Effects of solution treatment on mechanical properties and degradation of Mg-2Zn-0.5Nd-0.5Zr alloy

被引：14
作者：
Chen, Junxiu [1 ,2 ]
Wei, Sheng [1 ,2 ]
Tan, Lili [1 ]
Yang, Ke [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang, Liaoning, Peoples R China
来源：
MATERIALS TECHNOLOGY | 2019年 / 34卷 / 10期
关键词：
Magnesium alloy; solution treatment; mechanical properties; galvanic corrosion; degradation rate; BIODEGRADABLE MAGNESIUM SCREW; GRAIN-REFINEMENT; IN-VIVO; MG-2ZN-2GD ALLOY; CORROSION; BEHAVIOR; ND; MICROSTRUCTURE; EXTRUSION; STRENGTH;
D O I：
10.1080/10667857.2019.1603657
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Heat treatment is an effective method to reduce the degradation rate of biodegradable magnesium alloys, especially solution treatment. In this work, the effects of solution treatment on microstructure, mechanical properties and degradation behaviour of a Mg-2Zn-0.5Nd-0.5Zr alloy were investigated. The results showed that with increase of solution temperature, the grain size increased from 4-5 mu m for the untreated alloy to 25-30 mu m for the 550 degrees C treated alloy and the second phases were dissolved into the alloy matrix gradually. With increase of the temperature, both ultimate tensile strength and yield strength of the alloy were decreased, while the elongation was increased. The alloy after 500 degrees C solution treatment exhibited the lowest degradation rate and showed a uniform degradation process.
引用
收藏
页码：592 / 601
页数：10
相关论文
共 35 条
[1]   Review of Recent Developments in the Field of Magnesium Corrosion [J].
Atrens, Andrej ;
Song, Guang-Ling ;
Liu, Ming ;
Shi, Zhiming ;
Cao, Fuyong ;
Dargusch, Matthew S. .
ADVANCED ENGINEERING MATERIALS, 2015, 17 (04) :400-453
[2]   Effect of heat treatment on corrosion and electrochemical behaviour of AZ91D magnesium alloy [J].
Aung, NN ;
Zhou, W .
JOURNAL OF APPLIED ELECTROCHEMISTRY, 2002, 32 (12) :1397-1401
[3]   Effect of high-pressure torsion on grain refinement, strength enhancement and uniform ductility of EZ magnesium alloy [J].
Bryla, Krzysztof ;
Morgiel, Jerzy ;
Faryna, Marek ;
Edalati, Kaveh ;
Horita, Zenji .
MATERIALS LETTERS, 2018, 212 :323-326
[4]   Effect of minor content of Gd on the mechanical and degradable properties of as-cast Mg-2Zn-xGd-0.5Zr alloys [J].
Chen, Junxiu ;
Tan, Lili ;
Yu, Xiaoming ;
Yang, Ke .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2019, 35 (04) :503-511
[5]   Comparative study on effects of different coatings on biodegradable and wear properties of Mg-2Zn-1Gd-0.5Zr alloy [J].
Chen, Junxiu ;
Lu, Sihan ;
Tan, Lili ;
Etim, Iniobong P. ;
Yang, Ke .
SURFACE & COATINGS TECHNOLOGY, 2018, 352 :273-284
[6]   Comparative study of the effect of Nd and Y content on the mechanical and biodegradable properties of Mg-Zn-Zr-xNd/Y (x=0.5, 1, 2) alloys [J].
Chen, Junxiu ;
Tan, Lili ;
Etim, Iniobong P. ;
Yang, Ke .
MATERIALS TECHNOLOGY, 2018, 33 (10) :659-671
[7]   Effect of heat treatment on mechanical and biodegradable properties of an extruded ZK60 alloy [J].
Chen, Junxiu ;
Tan, Lili ;
Yang, Ke .
BIOACTIVE MATERIALS, 2017, 2 (01) :19-26
[8]   Examination of a biodegradable magnesium screw for the reconstruction of the anterior cruciate ligament: A pilot in vivo study in rabbits [J].
Diekmann, Julia ;
Bauer, Sylvie ;
Weizbauer, Andreas ;
Willbold, Elmar ;
Windhagen, Henning ;
Helmecke, Patrick ;
Lucas, Arne ;
Reifenrath, Janin ;
Nolte, Ingo ;
Ezechieli, Marco .
MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2016, 59 :1100-1109
[9]   Effect of Microstructure on Corrosion Behavior of Mg-Sr Alloy in Hank's Solution [J].
Dong, Jia-Hui ;
Tan, Li-Li ;
Ren, Yi-Bin ;
Yang, Ke .
ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2019, 32 (03) :305-320
[10]   In vitro and in vivo studies on a Mg-Sr binary alloy system developed as a new kind of biodegradable metal [J].
Gu, X. N. ;
Xie, X. H. ;
Li, N. ;
Zheng, Y. F. ;
Qin, L. .
ACTA BIOMATERIALIA, 2012, 8 (06) :2360-2374
1234