Effect of heat input on the microstructure of in-situ synthesized TiN-TiB/Ti based composite coating by laser cladding

被引：83
作者：
Li, M. [1 ]
Huang, J. [1 ]
Zhu, Y. Y. [1 ]
Li, Z. G. [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Shanghai Key Lab Mat Laser Proc & Modificat, Shanghai 200240, Peoples R China
来源：
SURFACE & COATINGS TECHNOLOGY | 2012年 / 206卷 / 19-20期
关键词：
Laser cladding; In situ; TiN-TiB/Ti based composite coating; WEAR-RESISTANCE; SURFACE MODIFICATION; FORMATION MECHANISM; TI-6AL-4V; BN; AL;
D O I：
10.1016/j.surfcoat.2012.03.082
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
In situ synthesized TiN and TiB particulate-reinforced metal matrix composite coating was formed on Ti-3Al-2V alloy by laser cladding with a Ti/h-BN powder mixture. The phase structure, microstructure, microhardness and wear performance of the composite clad layer were analyzed by optical microscope (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM), micro-hardness tester and wear testing machine. It has been found that the clad layer mainly consisted of alpha-Ti, TiN and Ti4N3-x at the laser power density of 120 W/mm(2); While, TiB and TiN were synthesized at the laser power densities of 150 and 180 W/mm(2). TiN and TiB were compared with dendrite and needle platelet type microstructures. The microhardness of laser clad layer was 800-1200 HV0.3 which was about 5 times of the substrate. The lost height of the substrate is almost 2 times of the clad layers. (c) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码：4021 / 4026
页数：6
相关论文
共 23 条
  • [11] Research on microstructure of in situ synthesized TiB2/Ni metal-ceramics composite coating
    Liu, S
    Zhang, WP
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 391 (1-2) : 146 - 150
  • [12] Friction and wear behavior of Ti following laser surface alloying with Si, Al and Si plus Al
    Majumdar, JD
    Mordike, BL
    Manna, I
    [J]. WEAR, 2000, 242 (1-2) : 18 - 27
  • [13] Microstructure and formation mechanism of in situ synthesized TiC/Ti surface MMC on Ti-6Al-4V by laser cladding
    Man, HC
    Zhang, S
    Cheng, FT
    Yue, TM
    [J]. SCRIPTA MATERIALIA, 2001, 44 (12) : 2801 - 2807
  • [14] Laser cladding of Ni-base composite coatings onto Ti-6Al-4V substrates with pre-placed B4C+NiCrBSi powders
    Meng, QW
    Geng, L
    Zhang, BY
    [J]. SURFACE & COATINGS TECHNOLOGY, 2006, 200 (16-17) : 4923 - 4928
  • [15] LASER CLADDING OF TI-6AL-4V WITH BN FOR IMPROVED WEAR PERFORMANCE
    MOLIAN, PA
    HUALUN, L
    [J]. WEAR, 1989, 130 (02) : 337 - 352
  • [16] Sliding wear resistance of metal matrix composite layers prepared by high power laser
    Ocelík, V
    Matthews, D
    De Hosson, JTM
    [J]. SURFACE & COATINGS TECHNOLOGY, 2005, 197 (2-3) : 303 - 315
  • [17] Selvan JS, 1999, MAT SCI ENG A-STRUCT, V260, P178, DOI 10.1016/S0921-5093(98)00964-2
  • [18] Laser clad TiC reinforced NiCrBSi composite coatings on Ti-6Al-4V alloy using a CW CO2 laser
    Sun, R. L.
    Lei, Y. W.
    Niu, W.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2009, 203 (10-11) : 1395 - 1399
  • [19] Analysis of the growth morphology of TiB and the microstructure refinement of the coatings fabricated on Ti-6Al-4V by laser boronizing
    Tian, Y. S.
    Zhang, Q. Y.
    Wang, D. Y.
    Chen, C. Z.
    [J]. CRYSTAL GROWTH & DESIGN, 2008, 8 (02) : 700 - 703
  • [20] Research progress on laser surface modification of titanium alloys
    Tian, YS
    Chen, CZ
    Li, ST
    Huo, QH
    [J]. APPLIED SURFACE SCIENCE, 2005, 242 (1-2) : 177 - 184
123