Viscosity, fragility and structure of Na2O-CaO-Al2O3-SiO2 glasses of increasing Al/Si ratio

被引:58
作者
Cheng, Jinshu [1 ]
Xiao, Zifan [1 ]
Yang, Kun [1 ]
Wu, Hao [1 ]
机构
[1] Wuhan Univ Technol, State Key Lab Silicate Mat Architectures, Wuhan 430070, Peoples R China
关键词
Viscosity; Workability; Kinetic fragility; Structure; HIGH-TEMPERATURE; IN-SITU; SILICATE; MELTS; RELAXATION; LIQUIDS; NA2O-AL2O3-SIO2; SIMULATIONS; DYNAMICS; BEHAVIOR;
D O I
10.1016/j.ceramint.2012.10.258
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The research and development of a new float glass with higher content of Al2O3 is essential for the commercial flat glass. The study on the workability and kinetic fragility of Na2O-CaO-Al2O3-SiO2 glass melts with different Al/Si ratios has been linked with the structure. The viscosities as a function of temperature for glass melts were derived on the basis of Vogel-Fulcher-Tamman (VFT) equation. Some characteristic temperatures and four characteristic temperature intervals of forming process in tin bath were estimated. The results showed that: adding 12 wt% Al2O3 substitute for SiO2, the melting point (Tm) increased about 35 K, entire temperature interval in tin bath narrowed down about 20 K, the shortening of workability was mainly reflected in the viscosity range of 10(5.75)-10(10) Pa s, the fragility index m increased by 15%. It reveals an inverse correlation between the workability and the fragility. The structural changes on the tetrahedron structural unit Q(n) (n=1, 2, 3, 4) were obtained by using Raman spectroscopy. Our analysis indicates that: the number of NBO reducing and a more polymerized structure with adding Al/Si ratios are responsible for the increase of viscosity; the tetrahedral distortion, a decrease of Q(3)/Q(2) in the Q(n) species, is responsible for the increase of fragility. (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码:4055 / 4062
页数:8
相关论文
共 35 条
[1]   RELAXATION IN LIQUIDS, POLYMERS AND PLASTIC CRYSTALS - STRONG FRAGILE PATTERNS AND PROBLEMS [J].
ANGELL, CA .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1991, 131 :13-31
[2]   Relaxation in glassforming liquids and amorphous solids [J].
Angell, CA ;
Ngai, KL ;
McKenna, GB ;
McMillan, PF ;
Martin, SW .
JOURNAL OF APPLIED PHYSICS, 2000, 88 (06) :3113-3157
[3]   CORRELATIONS OF THE NONEXPONENTIALITY AND STATE DEPENDENCE OF MECHANICAL RELAXATIONS WITH BOND CONNECTIVITY IN GE-AS-SE SUPERCOOLED LIQUIDS [J].
BOHMER, R ;
ANGELL, CA .
PHYSICAL REVIEW B, 1992, 45 (17) :10091-10094
[4]   Molecular dynamics simulations of soda-lime-silicate glasses [J].
Cormack, AN ;
Du, JC .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2001, 293 :283-289
[5]   Viscosity and glass transition temperature of hydrous float glass [J].
Del Gaudio, P. ;
Behrens, H. ;
Deubener, J. .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2007, 353 (03) :223-236
[6]   Kinetic fragility of hydrous soda-lime-silica glasses [J].
Deubener, J. ;
Behrens, H. ;
Mueller, R. ;
Zietka, S. ;
Reinsch, S. .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2008, 354 (42-44) :4713-4718
[7]  
ELDAMRAWI G, 1993, PHYS CHEM GLASSES, V34, P52
[8]  
English S, 1923, Part II J Soc Glass Technol, V8, P205
[9]   Viscosity and glass transition temperature of hydrous melts in the system CaAl2Si2O8-CaMgSi2O6 [J].
Giordano, D. ;
Potuzak, M. ;
Romano, C. ;
Dingwell, D. B. ;
Nowak, M. .
CHEMICAL GEOLOGY, 2008, 256 (3-4) :203-215
[10]   B-11 AND AL-27 NMR-STUDIES OF GLASSES IN SYSTEM NA2O-B2O3-AL2O3 (NABAL) [J].
GRESCH, R ;
MULLERWARMUTH, W ;
DUTZ, H .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1976, 21 (01) :31-40