Interfacial reactions and strength properties in dissimilar titanium alloy/Ni alloy/microduplex stainless steel diffusion bonded joints

被引:41
作者
Kundu, S. [1 ]
Sam, S. [1 ]
Chatterjee, S. [1 ]
机构
[1] Bengal Engn & Sci Univ, Dept Met & Mat Engn, Sibpur 711103, Howrah, India
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2013年 / 560卷
关键词
Intermetallics; Diffusion bonding; Microstructure; Scanning Electron Microscopy; Mechanical properties; PHASE-TRANSFORMATION; TI-6AL-4V ALLOY; INTERLAYER; MICROSTRUCTURE; 304-STAINLESS-STEEL;
D O I
10.1016/j.msea.2012.09.069
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The interfacial reactions and strength properties of a titanium alloy/ microduplex stainless steel diffusion bonded joint using Ni alloy as an intermediate materials was investigated in the temperature range of 800 to 950 degrees C for 75 min and at 950 degrees C for 15-90 min in vacuum. The microstructure observations at the stainless steel/Ni alloy interface indicate the presence of gamma-Fe layer up to 900 degrees C for 75 min and at 950 degrees C up to 45 min. Ni3Ti, NiTi and NiTi2 intermetallic layers were observed at the Ni alloy/titanium alloy interface at the same processing parameters and irregular shaped particles were present within the TiNi3 intermetallic layer. Beyond these processing parameters, the layer wise Fe-Ti or Fe-Cr-Ti base intermetallic compounds were observed at the microduplex stainless steel/Ni alloy interface. Maximum tensile strength of similar to 639.9 MPa and shear strength of similar to 477.8 MPa along with similar to 9.3% ductility were obtained for the diffusion couple processed at 900 degrees C for 75 min. (C) 2012 Published by Elsevier B.V.
引用
收藏
页码:288 / 295
页数:8
相关论文
共 31 条
[21]   Interfacial properties of diffusion bonded Ti-6Al-4V to AISI 304 stainless steel by inserting a Cu interlayer [J].
Ozdemir, N. ;
Bilgin, B. .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2009, 41 (5-6) :519-526
[22]   Phase transformation diffusion bonding of titanium alloy with stainless steel [J].
Qin, B ;
Sheng, GM ;
Huang, JW ;
Zhou, B ;
Qiu, SY ;
Li, C .
MATERIALS CHARACTERIZATION, 2006, 56 (01) :32-38
[23]   Fe-Ni-Ti (Iron-Nickel-Titanium) [J].
Raghavan, V. .
JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2010, 31 (02) :186-189
[24]   Production of intermetallic compounds from Ti/Al and Ni/Al multilayer thin films-A comparative study [J].
Ramos, A. S. ;
Vieira, M. T. ;
Morgiel, J. ;
Grzonka, J. ;
Simoes, S. ;
Vieira, M. F. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 484 (1-2) :335-340
[25]   Infrared brazing of Ti-6Al-4V and 17-4 PH stainless steel with a nickel barrier layer [J].
Shiue, R. K. ;
Wu, S. K. ;
Chan, C. H. ;
Huang, C. S. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (07) :2207-2217
[26]   High temperature deformation in Ti-5Al-2.5Sn alloy [J].
Tan, M. J. ;
Chen, G. W. ;
Thiruvarudchelvan, S. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 192 :434-438
[27]   The formation of intermetallics in dissimilar Ti6Al4V/copper/AISI 316 L electron beam and Nd:YAG laser joints [J].
Tomashchuk, I. ;
Sallamand, P. ;
Andrzejewski, H. ;
Grevey, D. .
INTERMETALLICS, 2011, 19 (10) :1466-1473
[28]   Diffusion bonding of AZ91 using a silver interlayer [J].
Torun, O. ;
Karabulut, A. ;
Baksan, B. ;
Celikyurek, I. .
MATERIALS & DESIGN, 2008, 29 (10) :2043-2046
[29]   Effect of phase transformation and intermetallic compounds on the microstructure and tensile strength properties of diffusion-bonded joints between Ti-6Al-4V and AISI 304L [J].
Vigraman, T. ;
Ravindran, D. ;
Narayanasamy, R. .
MATERIALS & DESIGN, 2012, 36 :714-727
[30]  
Villars P., 1995, HDB TERNARY PHASE AL, P8903