Effect of P5+ on spectroscopy and structure of Yb3+/Al3+/P5+ co-doped silica glass

被引：47

作者：

Xu, Wenbin ^{[1
,2
]}

Ren, Jinjun ^{[1
]}

Shao, Chongyun ^{[1
,3
]}

Wang, Xue ^{[1
,2
]}

Wang, Meng ^{[1
,2
]}

Zhang, Liyan ^{[1
]}

Chen, Danping ^{[1
]}

Wang, Shikai ^{[1
]}

Yu, Chunlei ^{[1
]}

Hu, Lili ^{[1
]}

机构：

[1] Chinese Acad Sci, Shanghai Inst Opt & Fine Mech, Key Lab Mat High Power Laser, Shanghai 201800, Peoples R China

[2] Univ Chinese Acad Sci, Beijing 100049, Peoples R China

[3] Shanghai Univ, Shanghai 200436, Peoples R China

来源：

JOURNAL OF LUMINESCENCE | 2015年 / 167卷

基金：

中国国家自然科学基金;

关键词：

Silica glass; Yb3+ spectroscopy; P5+ influences; Glass structure; EMISSION CROSS-SECTION; PHOSPHATE-GLASS; FIBER LASERS; YB3+; NMR; TEMPERATURE; FABRICATION; DEPENDENCE; AMPLIFIERS; AL2O3;

D O I：

10.1016/j.jlumin.2015.05.061

中图分类号：

O43 [光学];

学科分类号：

070207 ; 0803 ;

摘要：

Two series of silica glasses [(95.9-x)SiO2-4Al(2)O(3)-xP(2)O(5)-0.1Yb(2)O(3) (in mol%, x=0-10) and (92-y) SiO2-4Al(2)O(3)-4P(2)O(5)-yYb(2)O(3) (in mol%, y=0-0.2)] were prepared by sal-gel method combined with high-temperature sintering. The relationship between the glass structure and spectroscopic properties is investigated. Significant alterations in density, refractive index, absorption and emission cross sections, fluorescence lifetime, and scalar crystal field NJ are observed at a molar ratio of P5+/Al3+ =1 due to the transformation of P5+ structure type from AlPO4-like to PO4 units. This structural change is clearly observed in Raman spectra. In addition, NMR experimental results suggest that Yb3+ is mainly located in AlPO4-like but not SiO4 units at a molar ratio of P5+/Al3+ =1, and also Raman spectra reveals the presence of P=0 linkage in samples with molar ratio of P5+/Al3+ >1. This further demonstrates that it is due to the formation of P=0 site but not the simple addition of P2O5 in Yb3+/Al3+/P5+ co-doped silica glass to significantly decrease the absorption and emission cross sections of Yb3+. It reflects in the change of Yb3+ Stark splitting, and is revealed by the decline of Yb3+ asymmetry degree. (C) 2015 Elsevier B.V. All rights reserved.