Effect of geothermal waste on strength and microstructure of alkali-activated slag cement mortars

被引：28

作者：

Escalante-García, JI ^{[1
]}

Gorokhovsky, AV ^{[1
]}

Mendoza, G ^{[1
]}

Fuentes, AF ^{[1
]}

机构：

[1] CINVESTAV, Ctr Invest & Estudios Avanzados, Saltillo 25000, Coahuila, Mexico

来源：

CEMENT AND CONCRETE RESEARCH | 2003年 / 33卷 / 10期

关键词：

microstructure; EDX; mechanical properties; alkali-activated cement; geothermal silica waste;

D O I：

10.1016/S0008-8846(03)00133-9

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

Mortars of blast furnace slag replaced with 10% of a geothermal silica waste were cured for 90 days. The binder was activated by 6 wt.% Na2O equivalent of NaOH and water glass. The presence of the silica enhanced the formation of hydration products as shown by nonevaporable water (NEW) results. Backscattered electron images indicated that the microstructures of blended slag had less porosity than those of neat slag mortars and the interfacial zone between aggregate and hydration products was dense and of homogeneous composition similar to the matrix of hydration products. The main hydration products were C-S-H and for NaOH a hydrotalcite type phase was found as finely intermixed with the C-S-H. (C) 2003 Elsevier Ltd. All rights reserved.

引用

页码：1567 / 1574

页数：8

共 33 条

[1] Alkali activation of Australian slag cements [J].

Bakharev, T ;

Sanjayan, JG ;

Cheng, YB .

CEMENT AND CONCRETE RESEARCH, 1999, 29 (01) :113-120

[2] Effects of ultra-fine materials on workability and strength of concrete containing alkali-activated slag as the binder [J].

Collins, F ;

Sanjayan, JG .

CEMENT AND CONCRETE RESEARCH, 1999, 29 (03) :459-462

[3] Workability and mechanical properties of alkali activated slag concrete [J].

Collins, FG ;

Sanjayan, JG .

CEMENT AND CONCRETE RESEARCH, 1999, 29 (03) :455-458

[4]

DIAZ C, 1993, AM CERAM SOC BULL, V72, P81

[5]

DIAZ C, 1990, BOL SOC ESP CERAM V, V29, P181

[6] Effect of temperature on the hydration of the main clinker phases in Portland cements: Part II, blended cements [J].

Escalante-Garcia, JI ;

Sharp, JH .

CEMENT AND CONCRETE RESEARCH, 1998, 28 (09) :1259-1274

[7]

Escalante-Garcia JI, 1999, J AM CERAM SOC, V82, P3237

[8]

ESCALANTEGARCIA JI, 2003, IN PRESS J AM CERAM

[9]

FIDJESTOL P, 1997, LEAS CHEM CEMENT CON, P675

[10] Alkali-silica reaction (ASR) and alkali-carbonate reaction (ACR) in activated blast furnace slag cement (ABFSC) concrete [J].

Gifford, PM ;

Gillott, JE .

CEMENT AND CONCRETE RESEARCH, 1996, 26 (01) :21-26

← 1 2 3 4 →