The effect of copper and manganese on magnetic minor hysteresis loops in neutron irradiated Fe model alloys

Changes of magnetic minor hysteresis loops in pure Fe, Fe-1 wt% Mn, Fe-0.9 wt% Cu, and Fe-0.9 wt% Cu-1 wt% Mn model alloys after neutron irradiation have been studied. Minor-loop coefficients which are obtained from scaling relations between minor-loop parameters and in proportion to internal stress, were found to decrease in all model alloys after the irradiation to a fluence of 3.32 x 10(19) n cm(-2). The decrease of the coefficients is larger for alloys including Cu and is enhanced by 1 wt% Mn addition. Such decrease implying the reduction of internal stress during irradiation is in contrast with changes of yield strength after the irradiation that increase with Cu and Mn contents. A qualitative explanation was given on the basis of the preferential formation of Cu precipitates along pre-existing dislocations which reduces internal stress of the dislocations. (C) 2008 Elsevier B.V. All rights reserved.