Diffusion bonding of commercially pure titanium to low carbon steel using a silver interlayer

被引:128
作者
Atasoy, Euren [2 ]
Kahraman, Nizamettin [1 ]
机构
[1] Karabuk Univ, Tech Educ Fac, TR-78050 Karabuk, Turkey
[2] Tokat Adocim Cement Factory, TR-60100 Tokat, Turkey
关键词
diffusion welding/bonding; titanium; interlayer; microstructure;
D O I
10.1016/j.matchar.2008.01.015
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Titanium and low carbon steel plates were joined through diffusion bonding using a silver interlayer at various temperatures for various diffusion times. In order to determine the strength of the resulting joints, tensile-shear tests and hardness tests were applied. Additionally, optical, scanning electron microscopy examinations and energy dispersive spectrometry elemental analyses were carried out to determine the interface proper-ties of the joint. The work showed that the highest interface strength was obtained for the specimens joined at 850 degrees C for 90 min. It was seen from the hardness results that the highest hardness value was obtained for the interlayer material and the hardness values on the both sides of the interlayer decreased gradually as the distance from the joint increased. in energy dispersive spectrometry analyses, it was seen that the amount of silver in the interlayer decreased markedly depending on the temperature rise. In addition, increasing diffusion time also caused some slight decrease in the amount of silver. (C) 2008 Elsevier Inc. All rights reserved.
引用
收藏
页码:1481 / 1490
页数:10
相关论文
共 32 条
  • [1] Corrosion behaviour of commercially pure titanium shot blasted with different materials and sizes of shot particles for dental implant applications
    Aparicio, C
    Gil, FJ
    Fonseca, C
    Barbosa, M
    Planell, JA
    [J]. BIOMATERIALS, 2003, 24 (02) : 263 - 273
  • [2] Weldability of Al4C3-Al composites via diffusion welding technique
    Arik, H
    Aydin, M
    Kurt, A
    Turker, M
    [J]. MATERIALS & DESIGN, 2005, 26 (06) : 555 - 560
  • [3] Askeland RD, 1994, SCI ENG MAT, P110
  • [4] Electron beam welded high thickness Ti6A14V plates using filler metal of similar and different composition to the base plate
    Barreda, JL
    Santamaría, F
    Azpiroz, X
    Irisarri, AM
    Varona, JM
    [J]. VACUUM, 2001, 62 (2-3) : 143 - 150
  • [5] EKRAMI A, 2007, MAT SCI ENG A-STRUCT, V515, P93
  • [6] Effect of interface microstructure on the bond strength of the diffusion welded joints between titanium and stainless steel
    Ghosh, M
    Chatterjee, S
    [J]. MATERIALS CHARACTERIZATION, 2005, 54 (4-5) : 327 - 337
  • [7] Diffusion bonding of titanium to 304 stainless steel
    Ghosh, M
    Bhanumurthy, K
    Kale, GB
    Krishnan, J
    Chatterjee, S
    [J]. JOURNAL OF NUCLEAR MATERIALS, 2003, 322 (2-3) : 235 - 241
  • [8] Diffusion bonded transition joints of titanium to stainless steel with improved properties
    Ghosh, M
    Chatterjee, S
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 358 (1-2): : 152 - 158
  • [9] A new technology for diffusion bonding intermetallic TiAl to steel with composite barrier layers
    He, P
    Feng, JC
    Zhang, BG
    Qian, YY
    [J]. MATERIALS CHARACTERIZATION, 2003, 50 (01) : 87 - 92
  • [10] Effects of fluoride concentration and elastic tensile strain on the corrosion resistance of commercially pure titanium
    Huang, HH
    [J]. BIOMATERIALS, 2002, 23 (01) : 59 - 63