Preparation and properties of electrochromic iridium oxide thin film by sol-gel process

被引：76
|
作者：
Nishio, K [1 ]
Watanabe, Y [1 ]
Tsuchiya, T [1 ]
机构：
[1] Sci Univ Tokyo, Fac Ind Sci & Technol, Dept Mat Sci & Technol, Noda, Chiba 2788510, Japan
来源：
THIN SOLID FILMS | 1999年 / 350卷 / 1-2期
关键词：
sol-gel process; electrical properties and measurements; iridium; optical properties; oxides;
D O I：
10.1016/S0040-6090(99)00290-4
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We established a method for preparation of iridium oxide thin film by the sol-gel dip-coating process where iridium chloride was used as a starting material. The coating solution was prepared by reacting iridium chloride, ethanol and acetic acid. Iridium oxide coating was formed at 2.0 cm/min withdrawing rate. The coating films heat treated at 300 degrees C did not contain impurities. Iridium oxide crystallized at temperatures above 450 degrees C. Both crystalline and amorphous iridium oxide thin films showed electrochromism. The change in transmittance of the crystalline Ir2O3 film is larger than that of the amorphous Ir2O3 under the same experimental conditions. The transmittance of the crystalline thin firm (film thickness 200 nm, measured at 400 nm) decreased 13.0% on application of 3 V for 1 s. (C) 1999 Elsevier Science S.A. All rights reserved.
引用
收藏
页码：96 / 100
页数：5
相关论文
共 50 条
  • [21] Preparation and properties of VO2 thin films by a novel sol-gel process
    Zhang, Chenxi
    Cao, Wei
    Adedeji, Adetayo V.
    Elsayed-Ali, Hani E.
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2014, 69 (02) : 320 - 324
  • [22] Preparation of nanocrystalline nickel oxide thin films by sol-gel process for hydrogen sensor applications
    Soleimanpour, A. M.
    Jayatissa, Ahalapitiya H.
    MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2012, 32 (08): : 2230 - 2234
  • [23] Preparation of hydrophobic optical silica thin film with sol-gel method
    Ma, JH
    Wu, GM
    Cheng, YB
    Sun, Q
    Wang, JL
    Shen, J
    Wang, J
    ACTA PHYSICO-CHIMICA SINICA, 2001, 17 (12) : 1112 - 1116
  • [24] Effects of Cu doping on nickel oxide thin film prepared by sol-gel solution process
    Kim, Kyung Ho
    Takahashi, Chiaki
    Abe, Yoshio
    Kawamura, Midori
    OPTIK, 2014, 125 (12): : 2899 - 2901
  • [25] Fabrication and properties of zinc oxide thin film prepared by sol-gel dip coating method
    Kayani, Zohra Nazir
    Iqbal, Maryam
    Riaz, Saira
    Zia, Rehana
    Naseem, Shahzad
    MATERIALS SCIENCE-POLAND, 2015, 33 (03): : 515 - 520
  • [26] Evolution of hydrogen gas sensing properties of sol-gel derived nickel oxide thin film
    Soleimanpour, Amir M.
    Hou, Yue
    Jayatissa, Ahalapitiya H.
    SENSORS AND ACTUATORS B-CHEMICAL, 2013, 182 : 125 - 133
  • [27] Preparation and Transparent Conductivity of Antimony-Doped Tin Oxide Thin Film by Sol-gel Method
    Cai, Wei
    Fu, Chun-lin
    Gao, Jia-cheng
    Chen, Xue
    Deng, Xiao-ling
    PROCEEDINGS OF THE 7TH NATIONAL CONFERENCE ON CHINESE FUNCTIONAL MATERIALS AND APPLICATIONS (2010), VOLS 1-3, 2010, : 939 - +
  • [28] Preparation of LaCoO3 catalytic thin film by the sol-gel process and its NO decomposition characteristics
    Hwang, HJ
    Awano, M
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2001, 21 (10-11) : 2103 - 2107
  • [29] Structural and optical properties of BST thin films prepared by the sol-gel process
    Zhang, TJ
    Gu, HS
    Liu, JH
    MICROELECTRONIC ENGINEERING, 2003, 66 (1-4) : 860 - 864
  • [30] PREPARATION OF EPITAXIAL KTN THIN-FILMS BY SOL-GEL PROCESS
    BAO, DH
    KUANG, AX
    GU, HS
    WANG, SM
    CHINESE SCIENCE BULLETIN, 1993, 38 (07): : 550 - 553
12345