Preparation and properties of electrochromic iridium oxide thin film by sol-gel process

被引：76
|
作者：
Nishio, K [1 ]
Watanabe, Y [1 ]
Tsuchiya, T [1 ]
机构：
[1] Sci Univ Tokyo, Fac Ind Sci & Technol, Dept Mat Sci & Technol, Noda, Chiba 2788510, Japan
来源：
THIN SOLID FILMS | 1999年 / 350卷 / 1-2期
关键词：
sol-gel process; electrical properties and measurements; iridium; optical properties; oxides;
D O I：
10.1016/S0040-6090(99)00290-4
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We established a method for preparation of iridium oxide thin film by the sol-gel dip-coating process where iridium chloride was used as a starting material. The coating solution was prepared by reacting iridium chloride, ethanol and acetic acid. Iridium oxide coating was formed at 2.0 cm/min withdrawing rate. The coating films heat treated at 300 degrees C did not contain impurities. Iridium oxide crystallized at temperatures above 450 degrees C. Both crystalline and amorphous iridium oxide thin films showed electrochromism. The change in transmittance of the crystalline Ir2O3 film is larger than that of the amorphous Ir2O3 under the same experimental conditions. The transmittance of the crystalline thin firm (film thickness 200 nm, measured at 400 nm) decreased 13.0% on application of 3 V for 1 s. (C) 1999 Elsevier Science S.A. All rights reserved.
引用
收藏
页码：96 / 100
页数：5
相关论文
共 50 条
  • [1] Preparation of electrochromic tungsten oxide thin film by sol-gel process
    Nishio, K
    Sei, T
    Tsuchiya, T
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1999, 107 (03) : 199 - 203
  • [2] Preparation and properties of fully solid state electrochromic display thin film from sol-gel process
    Nishio, K
    Sei, T
    Tsuchiya, T
    SOL-GEL OPTICS IV, 1997, 3136 : 419 - 425
  • [3] Preparation and Characterization of Molybdenum Oxide Thin Films by Sol-Gel Process
    Sun Jiebing
    Xiong Rui
    Wang Shimin
    Tang Wufeng
    Tong Hua
    Shi Jing
    Journal of Sol-Gel Science and Technology, 2003, 27 (3) : 315 - 319
  • [4] Preparation and characterization of molybdenum oxide thin films by sol-gel process
    Sun, JB
    Xiong, R
    Wang, SM
    Tang, WF
    Tong, H
    Shi, J
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2003, 27 (03) : 315 - 319
  • [5] Preparation of ZnO thin film by sol-gel technique and its properties
    Zang, JC
    Gong, F
    Yan, JH
    Shan, BR
    Ye, JP
    Liu, M
    RARE METAL MATERIALS AND ENGINEERING, 2003, 32 : 564 - 567
  • [6] Synthesis and electrochromic study of sol-gel cuprous oxide nanoparticles accumulated on silica thin film
    Akhavan, O.
    Tohidi, H.
    Moshfegh, A. Z.
    THIN SOLID FILMS, 2009, 517 (24) : 6700 - 6706
  • [7] PREPARATION OF PZT THIN-FILMS BY SOL-GEL PROCESS AND PROPERTIES
    SAKAI, H
    TUCHIYA, T
    NIPPON SERAMIKKUSU KYOKAI GAKUJUTSU RONBUNSHI-JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1991, 99 (07): : 630 - 634
  • [8] Preparation of TiO2 nonparticle thin film with sol-gel process
    Shen, J
    Weng, ZN
    Zhang, YL
    Deng, ZS
    Yang, TH
    Wang, J
    Chen, LY
    THIRD INTERNATIONAL CONFERENCE ON THIN FILM PHYSICS AND APPLICATIONS, 1998, 3175 : 240 - 243
  • [9] Tungsten and Titanium Oxide Thin Films Obtained by the Sol-Gel Process as Electrodes in Electrochromic Devices
    Rizzuto, Carmen
    Barberi, Riccardo C.
    Castriota, Marco
    FRONTIERS IN MATERIALS, 2022, 9
  • [10] Optical, spectroelectrochemical and structural properties of sol-gel derived Ni-oxide electrochromic film
    Surca, A
    Orel, B
    Pihlar, B
    Bukovec, P
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1996, 408 (1-2) : 83 - 100
12345