Interface structure and mechanical properties of the brazed joint of TiC cermet and steel

被引：26

作者：

Feng, JC ^{[1
]}

Zhang, LX ^{[1
]}

机构：

[1] Harbin Inst Technol, Natl Key Lab Adv Welding Proc Technol, Harbin 150001, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2006年 / 26卷 / 07期

基金：

中国国家自然科学基金;

关键词：

TiC cermet; joining; interfaces; microstructure; strength;

D O I：

10.1016/j.jeurceramsoc.2005.01.043

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A commercially available Ag-Cu braze alloy foil with Zn Was Used to join TiC cermet and steel. According to the experimental observations, the interface structure is (Cu, Ni)/Ag (s.s.) + Cu (s.s.)/(Cu, Ni)/(Cu, Ni) + (Fe Ni) from TiC cermet to steel side. With increased brazing temperature or time, the amounts of (Cu, Ni) near the base metals/Ag-31Cu-23Zn interface and (Cu, Ni) + (Fe, Ni) near the Ag-31Cu-23Zn/steel interface increase, while the amount of Ag (s.s.) + Cu (s.s.) in the middle of the braze alloy decreases. The whole joining process consists of diffusion and solution among atoms of the braze alloy foil and base metals. The maximum shear strength is 120.7 MPa for the joint brazed at 850 degrees C for 10 min. (c) 2005 Elsevier Ltd. All rights reserved.

引用

页码：1287 / 1292

页数：6

共 50 条

[1] Effect of Bonding Temperature on Microstructure and Mechanical Properties of WC-Co/Steel Diffusion Brazed Joint
Haghshenas, Mahdi Shafiei
Parvin, Nader
Amirnasiri, Ali
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2018, 71 (03) : 649 - 658
[2] Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2
Wang, F. Z.
Wang, Q. Z.
Yu, B. H.
Xiao, B. L.
Ma, Z. Y.
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2011, 211 (11) : 1804 - 1809
[3] The Effect of W, Cr, Mo Content on the Microstructure and Mechanical Properties of the Weld Interface of TiC Cermet and Low-Carbon Steel
Wei, Wei
Huang, Zhiquan
Zhang, Haiyan
Guan, Shaokang
COATINGS, 2024, 14 (05)
[4] Brazing temperature and time effects on the mechanical properties of TiC cermet/Ag-Cu-Zn/steel joints
Zhang, L. X.
Feng, J. C.
He, P.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 428 (1-2): : 24 - 33
[5] Effect of Bonding Temperature on Microstructure and Mechanical Properties of WC–Co/Steel Diffusion Brazed Joint
Mahdi Shafiei Haghshenas
Nader Parvin
Ali Amirnasiri
Transactions of the Indian Institute of Metals, 2018, 71 : 649 - 658
[6] BRAZING OF TIC CERMET TO STEEL
Laansoo, A.
Kuebarsepp, J.
Vainola, V.
PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE OF DAAAM BALTIC INDUSTRIAL ENGINEERING, VOLS 1 AND 2, 2010, : 480 - 485
[7] Investigation on Wettability and Metallurgical and Mechanical Properties of Cemented Carbide and Steel Brazed Joint
Mousavi, S. A. A. Akbari
Sherafati, P.
Hoseinion, M. M.
MATERIALS AND MANUFACTURING TECHNOLOGIES XIV, 2012, 445 : 759 - +
[8] Numerical simulation of TiC cermet/iron joint brazed with Ag-Cu-Zn filler metal
Zhang, LX
Zhang, CP
Feng, JC
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 : 30 - 34
[9] Effect of Filler and Heat Treatment on the Physical and Mechanical Properties of the Brazed Joint between Carbide Tip and Steel
Winardi, Y.
Triyono
Wijayanta, A. T.
INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS FOR BETTER FUTURE 2016, 2017, 176
[10] Microstructure and shear strength of the brazed joint of Ti(C,N)-based cermet to steel
Ye Dameng
Xiong Weihao
Zhang Xiuhai
Qu Jun
Yao Zhenghua
RARE METALS, 2010, 29 (01) : 72 - 77

← 1 2 3 4 5 →