Microstructure and properties of the Si3N4/Si3N4 brazing joint

被引：0
|
作者：
Zhang, J [1 ]
Naka, N [1 ]
Zhou, Y [1 ]
Lei, TQ [1 ]
机构：
[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
来源：
MECHANICS AND MATERIAL ENGINEERING FOR SCIENCE AND EXPERIMENTS | 2001年
关键词：
Si3N4; ceramic; braze welding; interface; microstructure;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Si3N4 ceramic was brazed using a filler alloy Of (CUZn)(85)Til(5) alloy, and a Si3N4/Si3N4 joint with a high bonding strength was obtain under a suitable brazing condition. The brazing joint was composed of Cu2TiZn and Cu solution containing Titanium Silicide and Titanium Nitride. With increasing brazing temperature from 1123K to 1323K, the thickness of the reaction layer increased and the amount and size of the reactant increased. The addition of the Zn made the melting point of the filler alloy and the brazing temperature decreased, which improved the flowability and wettablility of the filler alloy. The evaporation of Zn was enhanced with increasing welding temperature. The shear strength of the Si3N4/Si3N4 joint increased with increasing welding temperature. The average shear strength of the joint reached 265 MPa when the welding temperature is 1223K.
引用
收藏
页码：222 / 225
页数：4
相关论文
共 50 条
  • [1] Interfacial microstructure of Si3N4/Si3N4 brazing joint with Cu-Zn-Ti filler alloy
    Zhang, J.
    Zhang, X. M.
    Zhou, Y.
    Naka, M.
    Svetlana, Atroshenko
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 495 (1-2): : 271 - 275
  • [2] Microstructure and Selected Properties of Si3N4
    Gabrisova, Zuzana
    Svec, Pavol
    Brusilova, Alena
    MANUFACTURING TECHNOLOGY, 2020, 20 (03): : 293 - 299
  • [3] Brazing of Si3N4 ceramic to copper
    ElSawy, AH
    Fahmy, MF
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1998, 77 (1-3) : 266 - 272
  • [4] Effect of bonding parameters on microstructure and properties of Si3N4/Si3N4 joint brazed by Cu-Zn-Ti filler alloy
    张杰
    周玉
    TransactionsofNonferrousMetalsSocietyofChina, 2005, (03) : 497 - 503
  • [5] Effects of β-Si3N4 Seeds Addition on Microstructure and Mechanical Properties of Porous Si3N4 Ceramics
    Yu, Fang-li
    Bai, Yu
    Du, Jun
    Yu, Ping-ping
    Wang, Jian-zhi
    Yang, Jian-feng
    ECO-MATERIALS PROCESSING AND DESIGN XIII, 2012, 724 : 201 - +
  • [6] EFFECT OF Ti CONTENT ON THE MICROSTRUCTURE AND PROPERTIES OF Si3n4/Si3N4 JOINT BRAZED USING Cu-Zn-Ti ALLOY
    M. Naka
    J. Zhang
    H. Y. Fang (1.Joining and Welding Research Institute
    ActaMetallurgicaSinica(EnglishLetters), 2000, (01) : 23 - 27
  • [7] Effect of bonding parameters on microstructure and properties of Si3N4/Si3N4 joint brazed by Cu-Zn-Ti filler alloy
    Zhang, J
    Naka, M
    Zhou, Y
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 (03) : 497 - 503
  • [8] Microstructure and mechanical properties of Si3N4/Si3N4 joint brazed with Ag-Cu-Ti plus SiCp composite filler
    He, Y. M.
    Zhang, J.
    Liu, C. F.
    Sun, Y.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (12): : 2819 - 2825
  • [9] Wettability of PdNi(Co)-Cr alloys on Si3N4 ceramic and joining of Si3N4 to Si3N4
    Xiong, Hua-Ping
    Chen, Bo
    Guo, Wan-Lin
    Ye, Lei
    WELDING IN THE WORLD, 2015, 59 (01) : 33 - 44
  • [10] Effect of bonding condition on microstructure and properties of the Si3N4/Si3N4 joint brazed using Cu-Zn-Ti filler alloy
    Zhang, J
    Fang, HY
    Zhou, Y
    Naka, M
    COMPOSITE MATERIALS III, 2003, 249 : 255 - 260
12345