Experimental Study on Phase Diagram in the Vicinity of X or W Phase in the Mg-Zn-Y Ternary System

被引:4
作者
Horiuchi, T. [1 ]
Ikee, H. [1 ]
Hamaya, A. [1 ]
Minamoto, S. [2 ]
Nomoto, S. [2 ]
Miura, S. [3 ]
机构
[1] Hokkaido Inst Technol, Grad Sch Engn, Div Mech Syst Engn, Teine Ku, 7-15-4-1 Maeda, Sapporo, Hokkaido 0068585, Japan
[2] ITOCHU Techno Solutions Corp CTC, Sci & Engn Syst Div, Chiyoda Ku, Tokyo 1006080, Japan
[3] Hokkaido Univ, Fac Engn, Div Mat Sci & Engn, Kita Ku, Sapporo, Hokkaido 0608628, Japan
来源
THERMEC 2011, PTS 1-4 | 2012年 / 706-709卷
关键词
Mg-Zn-Y; X phase; W phase; phase diagram; CALPHAD; PERIOD ORDERED STRUCTURE; MECHANICAL-PROPERTIES; ALLOY; STRENGTH;
D O I
10.4028/www.scientific.net/MSF.706-709.1170
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
To elucidate the phase equilibria in the vicinity of the X or W phase in the Mg-Zn-Y ternary system, five Mg-Zn-Y ternary alloys containing the X or W phase were prepared and isothermally heat-treated to reach thermodynamic equilibrium. The microstructure and chemical compositions of the equilibrium phases of the alloys were analyzed. Furthermore, the crystal structure of the W phase was investigated, and the liquidus temperatures of the alloys were examined using differential thermal analysis. The results showed that the X phase can be crystallized not by a eutectic reaction, as reported previously, but by a peritectic reaction. They also showed that the W phase has the Heusler-type crystal structure with a stoichiometric composition of Mg1Zn2Y1, and that Mg and Zn in the W phase can be substituted for each other. The Mg-Zn-Y ternary phase diagram was calculated using an assessed CALPHAD thermodynamic database based on the experimental results of the present study, and compared with a recently reported phase diagram.
引用
收藏
页码:1170 / +
页数:2
相关论文
共 15 条
[1]   Long-period ordered structure in a high-strength nanocrystalline Mg-1 at% Zn-2 at% Y alloy studied by atomic-resolution Z-contrast STEM [J].
Abe, E ;
Kawamura, Y ;
Hayashi, K ;
Inoue, A .
ACTA MATERIALIA, 2002, 50 (15) :3845-3857
[2]   THERMO-CALC & DICTRA, computational tools for materials science [J].
Andersson, JO ;
Helander, T ;
Höglund, LH ;
Shi, PF ;
Sundman, B .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2002, 26 (02) :273-312
[3]  
Fudetani S, 2009, MATER TRANS, V50, P349, DOI [10.2320/matertrans.L-MRA20088421, 10.2320/matertrans.L-MRA2008842]
[4]   Liquid-Solid Equilibrium and Intermediate Phase Formation during Solidification in Mg-1.3 at%Zn-1.7 at%Y Alloy [J].
Horiuchi, Toshiaki ;
Ono, Akemi ;
Yoshioka, Kentaro ;
Watanabe, Takero ;
Ohkubo, Kenji ;
Miura, Seiji ;
Mohri, Tetsuo ;
Tamura, Shigeyuki .
MATERIALS TRANSACTIONS, 2008, 49 (10) :2247-2253
[5]   Novel hexagonal structure and ultrahigh strength of magnesium solid solution in the Mg-Zn-Y system [J].
Inoue, A ;
Kawamura, Y ;
Matsushita, M ;
Hayashi, K ;
Koike, J .
JOURNAL OF MATERIALS RESEARCH, 2001, 16 (07) :1894-1900
[6]   Long period stacking structures observed inMg97Zn1Y2 alloy [J].
Itoi, T ;
Seimiya, T ;
Kawamura, Y ;
Hirohashi, M .
SCRIPTA MATERIALIA, 2004, 51 (02) :107-111
[7]   Rapidly solidified powder metallurgy Mg97Zn1Y2Alloys with excellent tensile yield strength above 600 MPa [J].
Kawamura, Y ;
Hayashi, K ;
Inoue, A ;
Masumoto, T .
MATERIALS TRANSACTIONS, 2001, 42 (07) :1172-1176
[8]  
Padezhnova E.M., 1982, RUSS METALL+, V4, P185
[9]  
Polmear I. J., 1994, MAT SCI TECHNOL, V42, P1
[10]   Elevated temperature behaviour of rapidly solidified magnesium alloys containing rare earths [J].
Sanchez, C ;
Nussbaum, G ;
Azavant, P ;
Octor, H .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 221 (1-2) :48-57