Synthesis of mordenite zeolite in absence of organic template

被引：62

作者：

Aly, Hisham M. ^{[1
]}

Moustafa, Moustafa E. ^{[1
]}

Abdelrahman, Ehab A. ^{[1
]}

机构：

[1] Benha Univ, Dept Chem, Fac Sci, Banha 13518, Egypt

来源：

ADVANCED POWDER TECHNOLOGY | 2012年 / 23卷 / 06期

关键词：

Nanoparticles; Mordenite; X-ray techniques; Crystal size; ZSM-5; ZEOLITES; CRYSTALS; MESOPOROSITY; DESILICATION; NANOCRYSTALS; RATIOS; SIZE;

D O I：

10.1016/j.apt.2011.10.003

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Mordenite is a zeolite that has been used as a selective adsorbent and as a catalyst. Mordenite zeolite with crystal diameter 65 nm and crystal length 7 mu m was successively synthesized in the absence of organic template by hydrothermal method at 180 degrees C for 5 days after stirring at high speed and aging in the synthesis mixture with the molar composition of 12Na(2)O:100SiO(2):2Al(2)O(3):500H(2)O. The produced samples were investigated using XRD, SEM, FT-IR, EDS, DTA/TG and BET surface area. The prepared sample, crystallized in needle shape crystals. Total (BET) surface area was 52.14 m(2)/g whereas, total pore volume was 0.2 cm(3)/g. Average pore diameter was 24.16 angstrom. Thermogravimetry analysis (DTA/TG) showed that, at room temperature to 800 degrees C, mordenite mass loss is 6%. (C) 2011 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.

引用

页码：757 / 760

页数：4

共 29 条

[1] Synthesis, characterization and catalytic activity of ZSM-5 zeolites having variable silicon-to-aluminum ratios [J].