Directional solidification of TiAl-Re-Si alloys with aligned γ/α2 lamellar microstructures

被引:54
|
作者
Yamanaka, T [1 ]
Johnson, DR [1 ]
Inui, H [1 ]
Yamaguchi, M [1 ]
机构
[1] Kyoto Univ, Dept Mat Sci & Engn, Sakyo Ku, Kyoto 6068501, Japan
基金
日本学术振兴会;
关键词
titanium aluminides; based on TiAl; phase diagram; mechanical properties at ambient temperature; crystal growth;
D O I
10.1016/S0966-9795(98)00129-0
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The effect of Re additions on the solidification behavior of Ti-Al-Re and Ti-Al-Re-Si alloys was investigated to determine if such additions would be compatible with a seeding technique developed previously to align the gamma/alpha(2) lamellar microstructure. Rhenium additions to TiAl were found to enlarge the primary beta composition range. Rhenium also tends to segregate to the beta-dendrite cores leading to the formation of the B2 phase. After the L + beta-->alpha peritectic reaction, Re tends to segregate to the interdendritic liquid. For the Ti-Al-Re alloys, the maximum Re content found in the lamellar microstructure was near 0.5 at% and the lamellar orientation in master alloys containing this amount of Re could successfully be grown from the seed material. However, such levels of Re had little effect on the measured yield stress either at room temperature or at 1000 degrees C and tensile failure usually occurred by the coalescence of microcracks that nucleated from large silicide particles. Finally, it was found that the gamma/alpha(2) lamellar microstructure of Ti-43.5Al-3Si-0.5Re can successfully be aligned by using an appropriately oriented seed even though beta is the primary solidification phase indicating that the alpha-phase from both the L + beta-->alpha peritectic and the L-->alpha + Ti5Si3 eutectic reactions must be continuous with that of the seed material. (C) 1999 Published by Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:779 / 784
页数:6
相关论文
共 50 条
  • [1] Creep deformation of TiAl-Si alloys with aligned γ/α2 lamellar microstructures
    Johnson, DR
    Masuda, Y
    Yamanaka, T
    Inui, H
    Yamaguchi, M
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (10): : 2463 - 2473
  • [2] Creep deformation of TiAl-Si alloys with aligned γ/α2 lamellar microstructures
    D. R. Johnson
    Y. Masuda
    T. Yamanaka
    H. Inui
    M. Yamaguchi
    Metallurgical and Materials Transactions A, 2000, 31 : 2463 - 2473
  • [3] Preparation of aligned lamellar microstructure in TiAl alloys by directional solidification with a seed technique
    Luo Wenzhong
    Shen Jun
    Li Qinglin
    Fu Hengzhi
    ACTA METALLURGICA SINICA, 2007, 43 (12) : 1287 - 1292
  • [4] Directional solidification of TiAl alloys with high Nb concentrations for aligning lamellar microstructures
    Inui, H
    Omiya, Y
    Johnson, DR
    NIOBIUM: HIGH TEMPERATURE APPLICATIONS, PROCEEDINGS, 2003, : 267 - 275
  • [5] Lamellar orientation control in γ-TiAl alloys by directional solidification
    Luo, Wenzhong
    Shen, Jun
    Min, Zhixian
    Fu, Hengzhi
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2009, 38 (10): : 1864 - 1869
  • [6] Lamellar Orientation Control in γ-TiAl Alloys by Directional Solidification
    Luo Wenzhong
    Shen Jun
    Min Zhixian
    Fu Hengzhi
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 (10) : 1864 - 1869
  • [7] Directional solidification of TiAl alloys for aligning lamellar microstructures and mechanical properties of directionally-solidified ingots
    Inui, H
    Johnson, DR
    Yamaguchi, M
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 1733 - 1738
  • [8] Directional solidification and microstructural control of the TiAl/Ti3Al lamellar microstructure in TiAl-Si alloys
    Johnson, DR
    Inui, H
    Yamaguchi, M
    ACTA MATERIALIA, 1996, 44 (06) : 2523 - 2535
  • [9] Creep of TiAl-Si alloys with aligned lamellar microstrucures
    Johnson, DR
    Masuda, Y
    Yamanaka, T
    Inui, H
    Yamaguchi, M
    GAMMA TITANIUM ALUMINIDES 1999, 1999, : 627 - 631
  • [10] Directional solidification and creep deformation of TiAl-Si alloys
    Yamanaka, T
    Johnson, DR
    Masuda, Y
    Inui, H
    Yamaguchi, M
    GAMMA TITANIUM ALUMINIDES 1999, 1999, : 295 - 300