The effect of sulfide on the aerobic corrosion of carbon steel in near-neutral pH saline solutions

被引：26
作者：
Sherar, B. W. A. [1 ]
Keech, P. G. [2 ]
Shoesmith, D. W. [3 ]
机构：
[1] Blade Energy Partners Ltd, Houston, TX 77084 USA
[2] Nucl Waste Management Org, Toronto, ON M4T 2S3, Canada
[3] Univ Western Ontario, Dept Chem, London, ON N6A 5B7, Canada
来源：
CORROSION SCIENCE | 2013年 / 66卷
基金：
加拿大自然科学与工程研究理事会;
关键词：
Mild steel; Polarization; SEM; Raman spectroscopy; Oxygen reduction; Microbiological corrosion; RAMAN-SPECTROSCOPY; HYDROGEN-SULFIDE; ARTIFICIAL GROUNDWATERS; ANAEROBIC CORROSION; EXTERNAL CORROSION; CYCLING CONDITIONS; LINE PIPE; CAST-IRON; PART; MINERALS;
D O I：
10.1016/j.corsci.2012.09.027
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Severe corrosion damage may occur when gas transmission pipelines are exposed, at disbanded coating locations, to trapped waters containing sulfide followed by secondary exposure to air. Aerobic corrosion with sulfide was investigated in a long-term corrosion experiment in which corrosion was monitored by measurement of the corrosion potential and polarization resistance obtained from linear polarization resistance measurements. The properties and composition of the corrosion product deposits formed were determined using scanning electron microscopy, energy dispersive X-ray analysis, and Raman spectroscopy. A switch from aerobic to aerobic-with-sulfide corrosion doubles the relative corrosion rate. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：256 / 262
页数：7
相关论文
共 50 条
  • [31] The effect of temperature on carbon steel corrosion under geological conditions
    El Mendili, Y.
    Abdelouas, A.
    Karakurt, G.
    Chaou, A. Ait
    Essehli, R.
    Bardeau, J. -F.
    Greneche, J. -M.
    APPLIED GEOCHEMISTRY, 2015, 52 : 76 - 85
  • [32] The Unified Mechanism of Corrosion in Aqueous Weak Acids Solutions: A Review of the Recent Developments in Mechanistic Understandings of Mild Steel Corrosion in the Presence of Carboxylic Acids, Carbon Dioxide, and Hydrogen Sulfide
    Kahyarian, Aria
    Brown, Bruce
    Nesic, Srdjan
    CORROSION, 2020, 76 (03) : 268 - 278
  • [33] Studies on corrosion of carbon steel in deaerated saline solutions in presence of scale inhibitor
    Andijani, I
    Turgoose, S
    DESALINATION, 1999, 123 (2-3) : 223 - 231
  • [34] Evolution from near-neutral to high-pH environments susceptible to stress corrosion cracking: The role of sulfate and bicarbonate
    Wang, Shidong
    Shirazi, Hamed
    Diao, Guijiang
    Farhat, Hanan
    Chen, Weixing
    CORROSION SCIENCE, 2024, 231
  • [35] Electrochemical behavior of API-X100 pipeline steel in NS4, near-neutral, and mildly alkaline pH simulated soil solutions
    Gadala, Ibrahim M.
    Alfantazi, Akram
    CORROSION SCIENCE, 2014, 82 : 45 - 57
  • [36] Formation and Structure of Sulfide Deposits on Carbon Steel Under Free Corrosion Potential
    Al-Qahtani, Noora
    Qi, Jiahui
    Abdullah, Aboubakr M.
    Laycock, Nicholas J.
    Ryan, Mary P.
    CORROSION, 2021, 77 (11) : 1164 - 1177
  • [37] Gamma-radiation-induced corrosion of carbon steel in neutral and mildly basic water at 150°C
    Daub, K.
    Zhang, X.
    Noel, J. J.
    Wren, J. C.
    CORROSION SCIENCE, 2011, 53 (01) : 11 - 16
  • [38] Hydrogen-facilitated anodic dissolution-type stress corrosion cracking of pipeline steels in near-neutral pH solution
    Gu, B
    Luo, J
    Mao, X
    CORROSION, 1999, 55 (01) : 96 - 106
  • [39] CORROSION INHIBITION OF CARBON STEEL IN SALINE SOLUTIONS BY GLUCONATE, ZINC SULPHATE AND CLAY ELUATE
    Ivusic, Franjo
    Lahodny-Sarc, Olga
    Stojanovic, Ivan
    TEHNICKI VJESNIK-TECHNICAL GAZETTE, 2014, 21 (01): : 107 - 114
  • [40] Environmentally assisted cracking of pipeline steels in CO2 containing environment at near-neutral pH
    Cabrini, Marina
    Lorenzi, Sergio
    Pastore, Tommaso
    Bolzoni, Fabio Maria
    CORROSION REVIEWS, 2017, 35 (4-5) : 309 - 323
12345