Surface modification of brucite and its application in flame retardant polypropylene composites

被引：0
|
作者：
Zhang, Ailing [1 ]
Chang, Ting [2 ]
Li, Sanxi [1 ]
Wang, Song [1 ]
Chi, Songjiang [1 ]
机构：
[1] Shenyang Univ Technol, Coll Sci, Shenyang 110870, Peoples R China
[2] Shenyang Univ Technol, Coll Mat Sci Engn, Shenyang 110870, Peoples R China
来源：
MATERIALS PROCESSING TECHNOLOGY II, PTS 1-4 | 2012年 / 538-541卷
关键词：
silane coupling agent; brucite; surface modification; activation index; limiting oxygen index; MAGNESIUM-HYDROXIDE;
D O I：
10.4028/www.scientific.net/AMR.538541214
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The surface modification of superfine brucite using silane coupling agent as a modifier was studied. The results of the best modified conditions show that the treated time is 1.5h, the treated temperature is 40 C, the content of silane coupling agent is 7wt%,the stirring speed is 600r/min. In this condition, the activation index up to 93.5%; the treated brucite particles filled into polypropylene(PP), the best tensile strength of 28.63MPa and the LOT of 30% is measured.
引用
收藏
页码：214 / +
页数：2
相关论文
共 50 条
  • [31] Chemical surface modification of lignin particle and its application as filler in the polypropylene composites
    Yeo, Jun-Seok
    Seong, Dong-Wook
    Hwang, Seok-Ho
    JOURNAL OF INDUSTRIAL AND ENGINEERING CHEMISTRY, 2015, 31 : 80 - 85
  • [32] Combustion behavior of intumescent flame retardant polypropylene composites
    Jiao, Chuanmei
    Zhang, Jun
    Zhang, Feng
    JOURNAL OF FIRE SCIENCES, 2008, 26 (05) : 455 - 469
  • [33] Tensile properties of polypropylene flame-retardant composites
    Liang, J. Z.
    POLYMER BULLETIN, 2012, 68 (03) : 803 - 813
  • [34] RHEOLOGICAL BEHAVIOR AND MICROSTRUCTURE OF FLAME RETARDANT POLYPROPYLENE COMPOSITES
    Jiang, Guo
    Liao, Kai
    Han, Juan-Juan
    Feng, De-Xian
    Huang, Han-Xiong
    PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION (IMECE 2010), VOL 10, 2012, : 415 - 418
  • [35] Tensile properties of polypropylene flame-retardant composites
    J. Z. Liang
    Polymer Bulletin, 2012, 68 : 803 - 813
  • [36] Mechanical properties of flame retardant filled polypropylene composites
    Tai, CM
    Li, RKY
    JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 80 (14) : 2718 - 2728
  • [37] Preparation of Nanoporous Nickel Phosphates with Surfactants and Application in Intumescent Flame Retardant Polypropylene Composites
    Nie, Shibin
    Dong, Xiang
    Wang, De-Yi
    Peng, Chao
    Liu, Lei
    PROCEEDINGS OF THE 2014 INTERNATIONAL CONFERENCE ON MATERIALS SCIENCE AND ENERGY ENGINEERING (CMSEE 2014), 2015, : 351 - 356
  • [38] Vinyl polysiloxane microencapsulated ammonium polyphosphate and its application in flame retardant polypropylene
    Zhu, Jianqiang
    Lu, Xin
    Yang, Huayu
    Xin, Zhong
    JOURNAL OF POLYMER RESEARCH, 2018, 25 (04)
  • [39] Vinyl polysiloxane microencapsulated ammonium polyphosphate and its application in flame retardant polypropylene
    Jianqiang Zhu
    Xin Lu
    Huayu Yang
    Zhong Xin
    Journal of Polymer Research, 2018, 25
  • [40] Flame surface modification of polypropylene film
    Strobel, M
    Branch, MC
    Ulsh, M
    Kapaun, RS
    Kirk, S
    Lyons, CS
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 1996, 10 (06) : 515 - 539
12345