Surface modification of brucite and its application in flame retardant polypropylene composites

被引：0
|
作者：
Zhang, Ailing [1 ]
Chang, Ting [2 ]
Li, Sanxi [1 ]
Wang, Song [1 ]
Chi, Songjiang [1 ]
机构：
[1] Shenyang Univ Technol, Coll Sci, Shenyang 110870, Peoples R China
[2] Shenyang Univ Technol, Coll Mat Sci Engn, Shenyang 110870, Peoples R China
来源：
MATERIALS PROCESSING TECHNOLOGY II, PTS 1-4 | 2012年 / 538-541卷
关键词：
silane coupling agent; brucite; surface modification; activation index; limiting oxygen index; MAGNESIUM-HYDROXIDE;
D O I：
10.4028/www.scientific.net/AMR.538541214
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The surface modification of superfine brucite using silane coupling agent as a modifier was studied. The results of the best modified conditions show that the treated time is 1.5h, the treated temperature is 40 C, the content of silane coupling agent is 7wt%,the stirring speed is 600r/min. In this condition, the activation index up to 93.5%; the treated brucite particles filled into polypropylene(PP), the best tensile strength of 28.63MPa and the LOT of 30% is measured.
引用
收藏
页码：214 / +
页数：2
相关论文
共 50 条
  • [1] Surface modification of magnesium hydroxide and its application in flame retardant polypropylene composites
    Xiaolang Chen
    Jie Yu
    Shaoyun Guo
    Shengjun Lu
    Zhu Luo
    Min He
    Journal of Materials Science, 2009, 44 : 1324 - 1332
  • [2] Surface modification of magnesium hydroxide and its application in flame retardant polypropylene composites
    Chen, Xiaolang
    Yu, Jie
    Guo, Shaoyun
    Lu, Shengjun
    Luo, Zhu
    He, Min
    JOURNAL OF MATERIALS SCIENCE, 2009, 44 (05) : 1324 - 1332
  • [3] Hydrophobic Modification of Ammonium Polyphosphate and Its Application in Flame Retardant Polypropylene Composites
    Liu Jianchao
    Xu Miaojun
    Li Bin
    CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE, 2015, 36 (06): : 1228 - 1235
  • [4] Mechanism on the surface modification of brucite inorganic flame retardant
    An, Yue
    Jing, Fengmei
    Ye, Jingyan
    Fushun Shiyou Xueyuan Xuebao/Journal of Fushun Petroleum Institute, 1998, 18 (02): : 22 - 24
  • [5] A new intumescent flame-retardant: preparation, surface modification, and its application in polypropylene
    Wang, Xingyi
    Li, Yuan
    Liao, Weiwei
    Gu, Jing
    Li, Dao
    POLYMERS FOR ADVANCED TECHNOLOGIES, 2008, 19 (08) : 1055 - 1061
  • [6] Mechanical Properties of Polypropylene-Based Flame Retardant Composites by Surface Modification of Flame Retardants
    Lee, Jinwoo
    Park, Jae Hyung
    Shim, Seung Bo
    Lee, Ji Eun
    POLYMERS, 2022, 14 (17)
  • [7] Microencapsulated ammonium polyphosphate and its application in the flame retardant polypropylene composites
    Chen, Man
    Tang, Mengqi
    Qi, Fei
    Chen, Xiaolang
    He, Weidi
    JOURNAL OF FIRE SCIENCES, 2015, 33 (05) : 374 - 389
  • [8] Surface Modification of Intumescent Flame Retardant and Its Application in Polypropylene with Excellent Fire Performance and Water Resistance
    Zheng, Xuqiang
    Deng, Mike
    Jia, Hao
    Chen, Xinyu
    Wang, Ruicheng
    Sun, Jun
    Li, Hongfei
    Gu, Xiaoyu
    Zhang, Sheng
    POLYMERS, 2025, 17 (03)
  • [9] Biomimetic flow field flame retardant modification of sisal fiber and its polypropylene composites
    Kang, Feng
    Han, Hongchang
    He, Dongtang
    Yi, Ming
    Wang, Ruifang
    Zhou, Ming
    INDUSTRIAL CROPS AND PRODUCTS, 2025, 223
  • [10] Study on the surface treatment of ammonium polyphosphate and its application in flame retardant polypropylene
    Hao, Jian-Wei
    Liu, Guo-Sheng
    Du, Jian-Xin
    Yang, Rong-Jie
    Qiu, Xue-Yang
    Zhu, Feng
    Beijing Ligong Daxue Xuebao/Transaction of Beijing Institute of Technology, 2009, 29 (06): : 556 - 559
12345