Synthesis of UV-curable silane-coupling agent as an adhesion promoter

被引：10
作者：
Kuo, Kuo-Huai [1 ]
Chiu, Wen-Yen [1 ,2 ,3 ]
Hsieh, Kuo-Huang [1 ,2 ]
机构：
[1] Natl Taiwan Univ, Dept Chem Engn, Taipei 106, Taiwan
[2] Natl Taiwan Univ, Inst Polymer Sci & Engn, Taipei 106, Taiwan
[3] Natl Taiwan Univ, Dept Mat Sci & Engn, Taipei 106, Taiwan
来源：
MATERIALS CHEMISTRY AND PHYSICS | 2009年 / 113卷 / 2-3期
关键词：
UV-curable silane; Adhesion; Black matrix; POLY(METHYL METHACRYLATE); GLASS; COMPOSITES; SILICA;
D O I：
10.1016/j.matchemphys.2008.08.071
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In color filter industry, a problem was found that the adhesion strength between glass substrate and black matrix was largely decreased after ITO sputtering process. in order to solve this problem, a new UV-curable silane-coupling agent (UV-SCA) was synthesized to be an adhesion promoter, which was synthesized by the reaction between the hydroxyl group of bisphenol A epoxy diacrylate and the isocyanate group of 3-(isocyanatopropyl)-triethoxysilane. The adhesion strength between glass substrate and black film, which was prepared from the carbon black photo-resist with or without the addition of UV-SCA, was determined by a tensile/compression strength tester, and the effect of UV-SCA on the adhesion strength before and after ITO sputtering process was also discussed. (C) 2008 Elsevier B.V. All rights reserved.
引用
收藏
页码：941 / 945
页数：5
相关论文
共 16 条
  • [1] Use of silanes and copolymers as adhesion promoters glass fiber/polyethylene composites
    Bikiaris, D
    Matzinos, P
    Prinos, J
    Flaris, V
    Larena, A
    Panayiotou, C
    [J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 80 (14) : 2877 - 2888
  • [2] Use of silane agents and poly(propylene-g-maleic anhydride) copolymer as adhesion promoters in glass fiber/polypropylene composites
    Bikiaris, D
    Matzinos, P
    Larena, A
    Flaris, V
    Panayiotou, C
    [J]. JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 81 (03) : 701 - 709
  • [3] The effect of organo-functional silanes on the adhesion of epoxide resins to ITO glass
    Chiang, TH
    Hsieh, TE
    [J]. JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2005, 19 (01) : 1 - 18
  • [4] ROLE OF TRIALKOXYSILANE FUNCTIONALIZATION IN THE PREPARATION OF ORGANIC-INORGANIC COMPOSITES
    COLTRAIN, BK
    LANDRY, CJT
    OREILLY, JM
    CHAMBERLAIN, AM
    RAKES, GA
    SEDITA, JS
    KELTS, LW
    LANDRY, MR
    LONG, VK
    [J]. CHEMISTRY OF MATERIALS, 1993, 5 (10) : 1445 - 1455
  • [5] INVERSE ORGANIC-INORGANIC COMPOSITE-MATERIALS .3. HIGH GLASS CONTENT NONSHRINKING SOL-GEL COMPOSITES VIA POLY(SILICIC ACID-ESTERS)
    ELLSWORTH, MW
    NOVAK, BM
    [J]. CHEMISTRY OF MATERIALS, 1993, 5 (06) : 839 - 844
  • [6] Preparation and characteristics of core-shell structure cobalt/silica nanoparticles
    Fu, Wuyou
    Yang, Haibin
    Hari-Bala
    Liu, Shikai
    Li, Minghui
    Zou, Guangtian
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2006, 100 (2-3) : 246 - 250
  • [7] Cyclophosphazene-containing polymers as imprint lithography resists
    Hagberg, Erik C.
    Hart, Mark W.
    Cong, Lianhui
    Allen, Christopher W.
    Carter, Kenneth R.
    [J]. JOURNAL OF INORGANIC AND ORGANOMETALLIC POLYMERS AND MATERIALS, 2007, 17 (02) : 377 - 385
  • [8] Structure and dynamics of a colloidal silica poly(methyl methacrylate) composite by C-13 and Si-29 MAS NMR spectroscopy
    Joseph, R
    Zhang, SM
    Ford, WT
    [J]. MACROMOLECULES, 1996, 29 (04) : 1305 - 1312
  • [9] ORGANIC-INORGANIC POLYMERIC HYBRIDS INVOLVING NOVEL POLY(HYDROXYMETHYLSILOXANE)
    LU, SX
    MELO, MM
    ZHAO, JQ
    PEARCE, EM
    KWEI, TK
    [J]. MACROMOLECULES, 1995, 28 (14) : 4908 - 4913
  • [10] Adhesion performance of an epoxy clear coat on aluminum alloy in the presence of vinyl and amino-silane primers
    Mohseni, M.
    Mirabedini, M.
    Hashemi, M.
    Thompson, G. E.
    [J]. PROGRESS IN ORGANIC COATINGS, 2006, 57 (04) : 307 - 313
12