Effects of Cure Temperature on Corrosion Property of vinyltriethoxysilane Films on Carbon Steel Surfaces

被引：3

作者：

Zhang Xu-ming ^{[1
]}

Wang Jiang-jun ^{[1
]}

Liu Chun-ming ^{[1
]}

Ying Yue-jun ^{[2
]}

机构：

[1] Northeastern Univ, Key Lab Anisotropy & Texture Mat MOE, Shenyang 110819, Peoples R China

[2] Shenyang Hangda Technol Co Ltd, Shenyang 11004, Peoples R China

来源：

ADVANCES IN MECHANICAL ENGINEERING, PTS 1-3 | 2011年 / 52-54卷

关键词：

vinyltriethoxysilane; carbon steel; cure; EIS; condensation; GALVANIZED STEEL; SILANE PRETREATMENTS; PROTECTION; COATINGS; ALUMINUM;

D O I：

10.4028/www.scientific.net/AMM.52-54.1947

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Silane treatment has been applied as a chromium free multi-metal surface treatment for its characteristics of corrosion protection, adhesion promotion and metal surface passivation. Vinyltriethoxysilane(VTES) hydrolysis solutions with the concentration of 4% and 10% were prepared, respectively. Morphologies and microstructures of the VIES films both before and after the corrosion test were observed with a scanning electron microscope (SEM), and effect of cure temperature on the corrosion resistance of silane film was studied combined with electrochemical impedance spectroscopy (EIS). The results showed that the cure temperature affects condensation states of silanol groups Si OH in silane films and promotes the forming of -Si-O-Si- network structure, and as a consequence influences the corrosion resistance of VIES films.

引用

页码：1947 / +

页数：2

共 50 条

[21] CORROSION OF CARBON STEEL BY HIGH-TEMPERATURE MERCURY
FLEITMAN, AH
ROMANO, AJ
KLAMUT, CJ
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1962, 109 (08) : C214 - C214
[22] Effect of Concentration and Temperature on Carbon Steel Corrosion Inhibition
Jafari H.
Akbarzade K.
Journal of Bio- and Tribo-Corrosion, 2017, 3 (1)
[23] MICROSTRUCTURE AND EROSION CORROSION PROPERTY OF CRNI ALLOYED COATING ON CARBON STEEL
Li, Shouying
Lin, Zhaoqing
SURFACE REVIEW AND LETTERS, 2024, 31 (08)
[24] Characterization and corrosion studies of laser-melted carbon steel surfaces
Agudelo, AC
Gancedo, JR
Marco, JF
Creus, MF
Gallego-Lluesma, E
Desimoni, J
Mercader, RC
APPLIED SURFACE SCIENCE, 1999, 148 (3-4) : 171 - 182
[25] Effects of temperature on acceleration and simulation of indoor corrosion test of Q235 carbon steel
Huang, Changxu
Su, Xuhong
Song, Qingqing
Wang, Xudong
ANTI-CORROSION METHODS AND MATERIALS, 2021, 68 (06) : 564 - 570
[26] Evaluation of the antimicrobial corrosion properties of electropolymerized poly(aniline-co-o-toluidine) films on carbon steel surfaces
Zhang, Si
Hu, Chuanbo
Hei, Xianling
Zhang, Xin
Lan, Bo
Yin, Huawei
Tang, Chengli
Zhao, Jie
Li, Tingzhen
SYNTHETIC METALS, 2025, 311
[27] Formation of protective corrosion films during CO2 corrosion of carbon steel
Dugstad, A
ADVANCES IN CORROSION CONTROL AND MATERIALS IN OIL AND GAS PRODUCTION, 1999, (26): : 70 - 76
[28] Effects of Deposition Temperature on Structure and Tribological Properties of Hydrogenated Carbon Films on Steel Balls
Fu Yu
Lu Yang
Yang Xiao-tian
Wang Yong-fu
Zhang Jun-yan
CHINA SURFACE ENGINEERING, 2018, 31 (04) : 113 - 121
[29] MICROSTRUCTURE EVOLUTION AND CORROSION PROPERTY OF MEDIUM-CARBON ALLOY STEEL AFTER HIGH-TEMPERATURE CARBURIZATION PROCESS
Deng Dewei
Niu Tingting
Liu Haiying
Zhang Lin
Sun Qi
SURFACE REVIEW AND LETTERS, 2016, 23 (05)
[30] The influence of temperature on the inhibition of carbon steel corrosion in acidic lignin
Yahya, Solhan
Othman, Norinsan Kamil
Daud, Abdul Razak
Jalar, Azman
Ismail, Roslina
ANTI-CORROSION METHODS AND MATERIALS, 2015, 62 (05) : 301 - 306

← 1 2 3 4 5 →