STRAIN PATH EFFECT ON IGSCC INITIATION AND OXIDATION OF ALLOY 182 EXPOSED TO PWR PRIMARY WATER

被引：0

作者：

Couvant, Thierry ^{[1
]}

Legras, Laurent ^{[1
]}

Ghys, Thierry ^{[1
]}

Gambier, Paul ^{[1
]}

Huin, Nicolas ^{[1
]}

Ilevbare, Gabriel ^{[2
]}

机构：

[1] EDF R&D, Ave Renardieres, F-77818 Moret Sur Loing, France

[2] EPRI, Palo Alto, CA USA

来源：

15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS | 2011年

关键词：

Alloy; 182; stress corrosion cracking; initiation; oxidation; strain path;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A detailed understanding of strain path effect on IGSCC and oxidation is of great importance for the prediction of the initiation of IGSCC of Ni base alloys 600, 182 and 690 exposed to the primary water of PWRs. In this study, a cross specimen was used in order to quantify the effect of a change of strain path on the strain localization and to increase the understanding of the contribution of the strain hardening and the strain localization at the grain boundaries on the precursors for initiation of SCC. Oxides were characterized using TEM and correlated with the local deformation.

引用

页码：1631 / 1643

页数：13

共 50 条

[31] Effect of dissolved hydrogen on the electrochemical behaviour of Alloy 600 in simulated PWR primary water at 290°C
Qiu, Yubing
Shoji, Tetsuo
Lu, Zhanpeng
CORROSION SCIENCE, 2011, 53 (05) : 1983 - 1989
[32] The effect of nano-sized precipitates on stress corrosion cracking propagation of Alloy 718 under constant loads in PWR primary water
Wang, Jiamei
Zhu, Tianyu
Wu, Yule
Chen, Kai
Guo, Xianglong
Ren, Quanyao
Li, Yuanming
Tang, Chuanbao
Yi, Hongpu
Ye, Liang
Xu, Shihao
Zhang, Jing
Tian, Wenxi
Zhang, Lefu
CORROSION SCIENCE, 2025, 242
[33] STRESS CORROSION CRACKING OF ALLOY 600 IN PWR PRIMARY WATER : INFLUENCE OF CHROMIUM, HYDROGEN AND OXYGEN DIFFUSION
Guerre, C.
Laghoutaris, P.
Chene, J.
Marchetti, L.
Molins, R.
Duhamel, C.
Sennour, M.
15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 1477 - 1488
[34] Stress Corrosion Cracking Behavior of Alloy 182 Weld in Pressurized Water Reactor Primary Water Environment at 325°C
Lima, L. I. L.
Schvartzman, M. M. A. M.
Figueiredo, C. A.
Bracarense, A. Q.
CORROSION, 2011, 67 (08)
[35] Dielectrostriction and Intergranular Stress Corrosion Cracking of Alloy 600 in PWR Primary Water
Devine, Thomas M.
CORROSION, PASSIVITY, AND ENERGY: A SYMPOSIUM IN HONOR OF DIGBY D. MACDONALD, 2013, 50 (31): : 91 - 97
[36] 2Effects of composition and microstructure on oxidation and stress corrosion cracking susceptibility of stainless steel claddings in hydrogenated PWR primary water
Cui, Tongming
Xu, Xinhe
Ma, Jiarong
Lu, Zhanpeng
Tang, Yuanjie
Zhang, Kun
Yang, Shuangliang
Zhong, Zhiming
Lozano-Perez, Sergio
Shoji, Tetsuo
JOURNAL OF NUCLEAR MATERIALS, 2021, 553 (553)
[37] Primary water stress corrosion cracking behavior of an Alloy 600/182 weld
Lim, Yun Soo
Hwang, Seong Sik
Kim, Sung Woo
Kim, Hong Pyo
CORROSION SCIENCE, 2015, 100 : 12 - 22
[38] The effect of strain path on the recrystallisation of an aluminium manganese alloy
Higginson, RL
RECRYSTALLIZATION AND GRAIN GROWTH, PTS 1 AND 2, 2004, 467-470 : 375 - 380
[39] Penetrative Internal Oxidation from Alloy 690 Surfaces and Stress Corrosion Crack Walls during Exposure to PWR Primary Water
Olszta, Matthew J.
Schreiber, Daniel K.
Thomas, Larry E.
Bruemmer, Stephen M.
15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 331 - 342
[40] Crack initiation of neutron-irradiated 304 L stainless steel in PWR primary water
Du, Donghai
Sun, Kai
Was, Gary S.
CORROSION SCIENCE, 2021, 193

← 1 2 3 4 5 →