Investigation of Thermal Shock Behavior of Plasma-Sprayed NiCoCrAlY/YSZ Thermal Barrier Coatings

被引：12
作者：
Jamali, Hossein [1 ]
Mozafarinia, Reza [1 ]
Shoja-Razavi, Reza [1 ]
Ahmadi-Pidani, Raheleh [1 ]
机构：
[1] Malek Ashtar Univ Technol, Dept Mat Engn, Esfahan, Iran
来源：
ADVANCED MANUFACTURING TECHNOLOGY, PTS 1-4 | 2012年 / 472-475卷
关键词：
Thermal barrier coating; YSZ; Thermal shock; Atmospheric plasma spraying; STABILIZED ZIRCONIA; BOND COAT; RESISTANCE;
D O I：
10.4028/www.scientific.net/AMR.472-475.246
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
ZrO2-8wt.%Y2O3 (8YSZ) thermal barrier coatings (TBCs) were deposited by atmospheric plasma spraying (APS) on NiCoCrAlY-coated Inconel 738LC substrates. The thermal shock behavior was investigated by quenching the samples in water with temperature of 20-25 degrees C from 950 degrees C. To study of failure mechanism results from thermal cycling, microstructural evaluation using scanning electron microscope (SEM), elemental analysis using energy dispersive spectroscopy (EDS) and phasic analysis using x-ray diffractometry (XRD) were done. The results revealed that failure of the TBC system was due to the spallation of ceramic top coat. Thermal mismatch stress was the major factor of TBC failure in thermal shock test.
引用
收藏
页码：246 / 250
页数：5
相关论文
共 20 条
  • [1] Characterization of modified thick thermal barrier coatings
    Ahmaniemi, S
    Tuominen, J
    Vippola, M
    Vuoristo, P
    Mäntylä, T
    Cernuschi, F
    Gualco, C
    Bonadei, A
    Di Maggio, R
    [J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2004, 13 (03) : 361 - 369
  • [2] High performance nanostructured ZrO2 based thermal barrier coatings deposited by high efficiency supersonic plasma spraying
    Bai, Y.
    Han, Z. H.
    Li, H. Q.
    Xu, C.
    Xu, Y. L.
    Wang, Z.
    Ding, C. H.
    Yang, J. F.
    [J]. APPLIED SURFACE SCIENCE, 2011, 257 (16) : 7210 - 7216
  • [3] Bose S., 2007, HIGH TEMPERATURE COA
  • [4] Failure Mechanism for Thermal Fatigue of Thermal Barrier Coating Systems
    Giolli, C.
    Scrivani, A.
    Rizzi, G.
    Borgioli, F.
    Bolelli, G.
    Lusvarghi, L.
    [J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2009, 18 (02) : 223 - 230
  • [5] Microcrack nucleation in thermal barrier coating systems
    Hille, T. S.
    Suiker, A. S. J.
    Turteltaub, S.
    [J]. ENGINEERING FRACTURE MECHANICS, 2009, 76 (06) : 813 - 825
  • [6] Chemical aspects of plasma spraying of zirconia-based thermal barrier coatings
    Ingo, Gabriel Maria
    de Caro, Tilde
    [J]. ACTA MATERIALIA, 2008, 56 (18) : 5177 - 5187
  • [7] Jamali H., 2011, 12 NAT CORR C TEHR I
  • [8] Manipulation of air plasma spraying parameters for the production of ceramic coatings
    Khan, A. Nusair
    Lu, J.
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (05) : 2508 - 2514
  • [9] Behavior of air plasma sprayed thermal barrier coatings, subject to intense thermal cycling
    Khan, AN
    Lu, J
    [J]. SURFACE & COATINGS TECHNOLOGY, 2003, 166 (01) : 37 - 43
  • [10] Integrity of nanostructured partially stabilized zirconia after plasma spray processing
    Lima, RS
    Kucuk, A
    Berndt, CC
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 313 (1-2): : 75 - 82
12