Optimization of synthesis of upconversion luminescence material NaYF4:Er3+,Yb3+ nanometer-phosphor by low-temperature combustion synthesis method

A kind of Er3+-Yb3+ co-doped natrium yttrium fluoride nanometer-phosphor sensitive to 980 nm was synthesized by the low-temperature combustion synthesis method, which expanded the application range of the low-temperature combustion synthesis (LCS) method which is always used in the synthesis of oxides and compound oxides. The synthesis conditions were optimized with orthogonal experiments and the optimum technological parameters were obtained. Intense upconversion emissions at 522, 540 and 653 nm corresponding to the H-2(11/2), S-4(3/2), and F-4(9/2) transitions to the I-4(15/2) ground state were observed when excited by continuous wave-length (CW) laser radiation at 980 nm. The effect of the carbamide amount on the phase formation and the luminescence intensity was analyzed. The average particle size of the sample was 30-40 nm.