Effect of solvents and thermal annealing on the morphology development of a novel block copolymer ionomer: a case study of sulfonated polystyrene-block-fluorinated polyisoprene

The morphologies of sulfonated polystyrene-block- fluorinated polyisoprene (s-PS-b-f-PI) were studied as functions of different kinds of solvents and thermal annealing, using transmission electron microscope microscopy (TEM), small angle X-ray scattering (SAXS) and intermediate angle X-ray diffraction (IMAXD). The film of the block copolymer ionomer with an acid form [sulfonated PS-b-fluorinated PI (sH-PS-b-f-PI)], which was cast from anhydrous tetrahydrofuran (THF), developed a well-ordered cylindrical morphology of the f-PI domains in the sH-PS matrix. The morphology was explained by the solubility parameter and the Bjerrum length. The morphology changed to that of a no long-range ordered structure, through thermal annealing. The result was different from the usual behavior of uncharged diblock copolymers and could have been due to the ionic cluster formation. The solution casting films of the block copolymer ionomer with a cesium neutralized form (sCsPS-b-f-PI) were obtained from the mixed solvent of THF/water (98/2, wt/wt) and DMSO. The ionic cluster formation in the film cast from the mixed solvent was hardly changed by annealing. The promotion of the ionic cluster formation by annealing was clearly observed in the film cast from DMSO. However, hindrance of microphase separation by the promotion of the ionic cluster formation was not confirmed in this study.